Polymer Property : 300% Modulus = 0.0111 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
300% Modulus	0.0111 GPa	1.61 ksi	DIN 53504
Huntsman IROGRANÂ® A 87 H 4615 Polyester-Based TPU-Injection Molding Grade Introduction: IROGRAN A 87 H 4615 is a thermoplastic polyester- polyurethane for injection molding applications. Additional characteristics of the product are very short cycle times and high dimensi..
300% Modulus	0.0111 GPa @Temperature 145 Â°C, Time 2100 sec	1.61 ksi @Temperature 293 Â°F, Time 0.583 hour	ASTM D412
LG Chemical SBR 1739 High Acrylonitrile Polymer Description: SBR 1739 is an oil extended cold polymerization SBR with 37.5 parts of Low PCA (PolyCyclic Aromatic) oil and styrene-butadiene copolymer of 40% bound styrene. Raw materials for this p..
300% Modulus	0.0111 GPa @Temperature 145 Â°C, Time 2100 sec	1.61 ksi @Temperature 293 Â°F, Time 0.583 hour	ASTM D412
LG Chemical SBR 1789 High Acrylonitrile Polymer Description: SSBR 1789 is an oil extended cold polymerization SBR with 37.5 parts of Low PCA (RAE type) oil and styrene-butadiene copolymer of 40% bound styrene. Raw materials for this product are ..
300% Modulus	0.0111 GPa	1.61 ksi	ASTM D412
UBE UBEPOL VCR303 Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C) Description: UBEPOL-VCR is a new type of synthetic rubber system developed by UBE's original technology. UBEPOL-VCR consists of micro-dispersed syndiotactic 1,2-polybutadiene (SPB) with high mel..