Polymer Property : Modulus of Elasticity = 8.27 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	8.27 GPa @Thickness 1.57 mm	1200 ksi @Thickness 0.0620 in	CW; ASTM D229
Industrial Laminates/Norplex NP555 Carbon Fiber (discontinued **) Description: NP555 is composed of carbon fiber fabric and a phenolic resin system. It has excellent moisture resistance and physical properties. This material was designed to replace asbestos vane m..
Modulus of Elasticity	8.27 GPa @Thickness 1.57 mm	1200 ksi @Thickness 0.0620 in	CW; ASTM D229
Industrial Laminates/Norplex NP193M Synthetic Fabric Base Grade Description: 17 oz. aramide and â€œsoft glassâ€ fibers are combined to make a fabric that is stronger than pure aramide and less abrasive than glass fabrics. This material is impregnated with..
Modulus of Elasticity	8.27 GPa @Thickness 1.57 mm	1200 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP193M Synthetic Fabric Base Grade Description: 17 oz. aramide and â€œsoft glassâ€ fibers are combined to make a fabric that is stronger than pure aramide and less abrasive than glass fabrics. This material is impregnated with..
Modulus of Elasticity	8.27 GPa @Thickness 1.57 mm	1200 ksi @Thickness 0.0620 in	CW; ASTM D229
Industrial Laminates/Norplex NP193P Synthetic Fabric Description: 17 oz. aramid and "soft glass" fibers are combined to make a fabric that is stronger than pure aramid and less abrasive than glass fabrics. This material is impregnated with a high temp..
Modulus of Elasticity	8.27 GPa @Thickness 1.57 mm	1200 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP193P Synthetic Fabric Description: 17 oz. aramid and "soft glass" fibers are combined to make a fabric that is stronger than pure aramid and less abrasive than glass fabrics. This material is impregnated with a high temp..
Modulus of Elasticity	8.27 GPa @Thickness 1.57 mm	1200 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP313 Cotton Fabric Description: Canvas phenolic laminate with molybdenum disulfide lubricant. Mechanical properties slightly lower than NP310.Thickness Tested: 0.062", 0.125" & 0.500"
Modulus of Elasticity	8.27 GPa @Thickness 1.57 mm	1200 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP315 Cotton Fabric Description: Canvas phenolic laminate with graphite added as a solid lubricant. This material has improved wear properties under certain conditions. Material is conductive to electricity and should ..
Modulus of Elasticity	8.27 GPa @Thickness 1.57 mm	1200 ksi @Thickness 0.0620 in	CW; ASTM D229
Industrial Laminates/Norplex NP320E Cotton Fabric Description: Similar to NP320 with improved moisture resistance. Suitable for electrical applications in moderate humidity conditions.Thickness Tested: 0.062", 0.125", and 0.500â€
Modulus of Elasticity	8.27 GPa @Thickness 1.57 mm	1200 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP611 Paper Base Laminate Description: Hot punching general-purpose phenolic grade. Mechanical properties approach those of NP610 with improved electrical properties and moisture resistance.Thickness Tested: 0.062", 0 125" a..
Modulus of Elasticity	8.27 GPa @Thickness 1.57 mm	1200 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP615 Paper Base Laminate Description: Room temperature punching and shearing grade up to .125" thick. More flexible and lower mechanical properties than NP611. NP615 is produced with high resin content melamine impregnated ..
Modulus of Elasticity	8.27 GPa @Thickness 1.57 mm	1200 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP664 Paper Base Laminate Description: Low cost room temperature punching grade with mechanical and electrical properties similar to NP612. This version is made with pigment cover plies on the surface.Thickness Tested: 0.062..