Polymer Property : Modulus of Elasticity = 8.96 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	8.96 GPa @Thickness 1.57 mm	1300 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP555 Carbon Fiber (discontinued **) Description: NP555 is composed of carbon fiber fabric and a phenolic resin system. It has excellent moisture resistance and physical properties. This material was designed to replace asbestos vane m..
Modulus of Elasticity	8.96 GPa @Thickness 1.57 mm	1300 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP319 Cotton Fabric Base Laminate Description: Bleached canvas combined with phenolic resin and graphite lubricant. Better moisture resistance and machining characteristics than NP315.
Modulus of Elasticity	8.96 GPa @Thickness 1.57 mm	1300 ksi @Thickness 0.0620 in	CW; ASTM D229
Industrial Laminates/Norplex NP320 Cotton Fabric Description: Fine weave (less than 4 ounce/square yard) cotton fabric commonly called linen, combined with phenolic resin to provide better machining than NP310. For smaller and more intricate shape..
Modulus of Elasticity	8.96 GPa @Thickness 1.57 mm	1300 ksi @Thickness 0.0620 in	CW; ASTM D229
Industrial Laminates/Norplex NP342 Cotton Fabric Description: Fine weave canvas phenolic material with fabric construction weight intermediate to NP310 and NP320. Designed for better machining than grade NP310 and lower cost than NP320.Thickness T..
Modulus of Elasticity	8.96 GPa @Thickness 1.57 mm	1300 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP630 Paper Base Laminate Description: Machining grade with good electrical properties and moisture resistance. Low cold flow with good dimensional stability. Thickness Tested: 0.062", 0.125", and 0.500"
Modulus of Elasticity	8.96 GPa @Thickness 1.57 mm	1300 ksi @Thickness 0.0620 in	CW; ASTM D229
Industrial Laminates/Norplex NP639 Paper Base Laminate Description: Economical paper reinforced laminate developed with capacity to withstand temperatures to 150Â° C without blistering. High compressive strength and low moisture absorption.Thickness T..