Polymer Property : Flexural Strength = 23500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	162 MPa	23500 psi	ASTM D 790
SABIC Innovative Plastics Enduran 7062X PBT+PET (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength	162 MPa	23500 psi	ASTM D790
Kotec Carbotex KG-30MRA Polycarbonate, 30% Glass Fiber Reinforced Features: Glass fiber 30% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E ..
Flexural Strength	162 MPa	23500 psi	ASTM D790
Kotec Carbotex KGN-30MRA Polycarbonate, Flame Retardant, 30% Glass Fiber Reinforced Features: Glass fiber 30% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E ..
Flexural Strength	162 MPa	23500 psi	2 mm/min; ISO 178
Ineos ABS LustranÂ® SAN GF20 Glass Fiber Reinforced
Flexural Strength	162 MPa	23500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL PX5558 PPE+PS 30% glass reinforced, high flow PPO.
Flexural Strength	162 MPa	23500 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Stat-kon AE004E ABS LNP* Stat-Kon* AE004E is an ABS compound containing Glass Fiber. Characteristics of this grade are Statically Conductive and Easy Molding.This data was supplied by SABIC-IP for the Americas region...
Flexural Strength	162 MPa	23500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON ZX08301 PPE (Asia Pacific) Stat-Kon* ZX08301 compound is a high heat compounds with ESD safe and low warpage performance suitable for use in Semiconductor Packaging Applications.
Flexural Strength	162 MPa	23500 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP DF004E PC LNP THERMOCOMP* DF004E is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding.
Flexural Strength	162 MPa	23500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP GX05482 PSU LNP* THERMOCOMP* GX05482 is a compound based on Polysulfone resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant.
Flexural Strength	162 MPa	23500 psi	ASTM D790
Techmer ES PlastiblendÂ® TPX-HTN-000CB 15% Glass Filled Availability: North AmericaForms: Pellets Filler/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightFeatures: High Heat ResistanceInformation provided by TP Composites, Inc.
Flexural Strength	162 MPa	23500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP VERTON MV007SU PP (Europe-Africa-Middle East) LNP* VERTON * MV007SU is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized, UV Stabilizedl.
Flexural Strength	162 MPa	23500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP VERTON MV007SUP PP (Europe-Africa-Middle East) LNP* VERTON* MV007SUP is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized, UV Stabilized.
Flexural Strength	162 MPa	23500 psi	2 mm/min; ISO 178
Sax Polymers SAXAMID 126K6 Nylon 6, 30% Glass Filled SAXAMID 126K6 is a 30% glass beads filled polyamide 6 injection-molding-grade. It is characterized by dimensional stability, low warpage and good surface quality.Information provided by SAX Polymers..
Flexural Strength	162 MPa	23500 psi	ISO 178
SABIC Innovative Plastics LNP VERTON NV003E PC+ABS (Asia Pacific) LNP* Verton* NV003E is a compound based on PC+ABS Blend resin containing Long Glass Fiber. Added features of this material include: Easy Molding.
Flexural Strength	162 MPa	23500 psi	ISO 178
SABIC Innovative Plastics LNP STAT-KON DE003M PC LNP* STAT-KON* DE003M is a compound based on Polycarbonate containing 15% Milled Carbon Fiber. Added feature of this grade is: Electrically Conductive.
Flexural Strength	162 MPa	23500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL EM7430 PPE+PS 30% glass reinforced, high flow PPO. Automotive. Energy management material.
Flexural Strength	162 MPa	23500 psi	ASTM D790
Westlake Plastics Absylux® CN-F Acrylonitrile-Butadiene-Styrene (conductive) Non-sloughing, carbon-fiber-filled material with high strength and stiffness; easily machined.Information provided by Westlake Plastics.
Flexural Strength	162 MPa @Temperature 23.0 °C	23500 psi @Temperature 73.4 °F	EN ISO 178
Ensinger TECASINT 5011 Polyimide (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel..
Flexural Strength	162 MPa @Temperature 150 °C	23500 psi @Temperature 302 °F	ASTM D790
DuPont Performance Polymers VESPEL TP-8541 Polyimide Thermoplastic parts from filled PI (polyimide) for high mechanical properties and impact performance in high temperature environmentsInformation provided by DuPont Performance Polymers
Flexural Strength	162 MPa	23500 psi	ASTM D790
Applied Composites 185 Polyester SMC Industry Application: TransportationProduct Application: Lawn and GardenDistinct Features: Limited PigmentabilityInformation provided by Applied Composites Corporation.
Flexural Strength	162 MPa	23500 psi	ASTM D790
Gharda Chemicals Gafone™ B2315GF Polysupersulfone (PSS) (discontinued **) Characteristics: Excellent Dimensional properties Transparent Improved Impact Strength and Toughness as compared to PES Excellent Hydorlytic Stability High Stress Cracking Resistance Good Chemical..