- Polymer Property : Flexural Strength = 24100 psi
Polymer Property : Flexural Strength = 24100 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| Ravago Manufacturing Americas Hylex® P1010G30 HB Polycarbonate, 30% Fiberglass Reinforced Information provided by Ravago. |
|||
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| Ravago Manufacturing Americas Hylex® P1310G30 HB Polycarbonate, 30% Fiberglass Reinforced, UV Stabilized Information provided by Ravago. |
|||
| Flexural Strength | 166 MPa @Temperature 22.0 °C |
24100 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Menzolit Menzolit® SMC 0900 Unsaturated Polyester UP SMC 0900 is a special SMC for use within a chemical aggressive environment. The glass level is selected to combine good mouldability with good strength and stiffness properties. The product is espec.. |
|||
| Flexural Strength | 166 MPa | 24100 psi | 5 mm/min; ISO 178 |
| Gromax BFM30-EL04B2 Nylon 6 30% Mineral Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
| Flexural Strength | 166 MPa | 24100 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRILOY DF206XXH PC LNP* LUBRILOY* DF206XXH is a compound based on Polycarbonate containing 30% Glass Fiber, Proprietary Lubricant. Added features of this grade include: Wear Resistant, Healthcare. |
|||
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP DF004ER PC LNP THERMOCOMP* DF004ER is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding. Mold Release. |
|||
| Flexural Strength | 166 MPa | 24100 psi | ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP DF004ER PC LNP THERMOCOMP* DF004ER is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding. Mold Release. |
|||
| Flexural Strength | 166 MPa | 24100 psi | ASTM D 790 |
| SABIC Innovative Plastics Noryl GTX GTX870 PPE+PA6 (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| SABIC Innovative Plastics NORYL GTX GTX870 PPE+PA6 (Asia Pacific) |
|||
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| SABIC Innovative Plastics NORYL GTX870 PPE+PA6 (Asia Pacific) |
|||
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| SABIC Innovative Plastics NORYL APS430 PPE+PPS (Asia Pacific) |
|||
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| SABIC Innovative Plastics NORYL GTX APS430 PPE+PPS (Asia Pacific) PPE + PPS GF 30%, FR V-0 |
|||
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| SABIC Innovative Plastics NORYL GTX APS440 PPE+PPS (Asia Pacific) PPE+PPS, GF40%, FR V-0 |
|||
| Flexural Strength | 166 MPa | 24100 psi | ISO 178 |
| Polyplastics Duranex® 7390W Polybutylene Terephthalate (PBT), Super low warpage, GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| Flexural Strength | 166 MPa | 24100 psi | ISO 178 |
| Polyplastics Duranex® CN5315 Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, 15% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| Ensinger Tecapeek® XP-119G Compression Molded PEEK Compound, 10% Carbon Fiber with 5% Graphite Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| Ashley Polymers Ashlene® P126T PBT Polyester, 30% Glass Reinforced Impact modified, 30% glass reinforced.Data provided by the manufacturer |
|||
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| A. Schulman ComAlloy Hiloy® 263 Glass Reinforced, Modified SMA Data provided by the manufacturer, ComAlloy International Company.35% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| SABIC Innovative Plastics NORYL APS440 PPE+PPS (Asia Pacific) |
|||
| Flexural Strength | 166 MPa | 24100 psi | ASTM D790 |
| Resinoid 7051 SS Phenolic Molding, Glass Reinforced Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance |
|||