Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 297 MPa | 43100 psi | ASTM D-790 |
PlastiComp Complet® LCF30-PPS Polyphenylene Sulfide, 30% Long Carbon Fiber Reinforced Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Polyphenylene Sulfide with 30% long carbon fiber reinforcementInformation provided by .. |
|||
Flexural Strength | 297 MPa | 43100 psi | ASTM D-790 |
PlastiComp Complet® LGF40 - PA66 MT Nylon 66, 40% Long Glass Fiber Reinforced, Impact Modified Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 66 with 40% long glass fiber reinforcementImpact modifiedInformation provided by.. |
|||
Flexural Strength | 297 MPa | 43100 psi | ASTM D790 |
PlastiComp Complet® LGF40-PA66 MT 40% Long Glass Fiber This compound complies with European Union Directive 2002/95/EC Restriction of Hazardous Substances (RoHS).Information provided by PlastiComp, Inc. |
|||
Flexural Strength | 297 MPa | 43100 psi | |
SGL Carbon Group SIGRAFIL C® filled PEEK Information provided by SGL Carbon Group |
|||
Flexural Strength | 297 MPa | 43100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Stat-kon EE008E PEI LNP STAT-KON* EE008E is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas r.. |
|||
Flexural Strength | 297 MPa | 43100 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF33 HS L 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant, UV Stabilizer and Heat StabilizerFeatures: Heat Stabilized, Good UV.. |
|||
Flexural Strength | 297 MPa | 43100 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF33 HS L BK 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Heat Stabilized and LubricatedAppearanc.. |
|||
Flexural Strength | 297 MPa | 43100 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF007SXQ PA 66 LNP THERMOCOMP* RF007SXQ is a compound based on Nylon 66 resin containing 35% Glass Fiber. Added features of this material include: Heat Stabilized, Hydrolysis Resistant. |
|||
Flexural Strength | 297 MPa | 43100 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON RE0039 PA 66 LNP STAT-KON* RE0039 is a compound based on Nylon 66 resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant. |
|||
Flexural Strength | 297 MPa | 43100 psi | ISO 178 |
SABIC Innovative Plastics LNP VERTON PV007 PA 6 LNP* VERTON* PV007 is a compound based on Nylon 6 resin containing 35% Long Glass Fiber. Added feature of this grade is: Structural. |
|||
Flexural Strength | 297 MPa | 43100 psi | ASTM Test |
BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Dry) Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also.. |
|||
Flexural Strength | 297 MPa @Temperature -40.0 °C |
43100 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Conditioned) Ultramid 8333G HI is a 14% glass reinforced, impact modified PA6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a
balance of st.. |
|||
Flexural Strength | 297 MPa | 43100 psi | ISO 178 |
SABIC Innovative Plastics LNP VERTON PV007 PA 6 (Asia Pacific) LNP* Verton* PV007 is a compound based on Nylon 6 resin containing Long Glass Fiber. |
|||
Flexural Strength | 297 MPa | 43100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP VERTON RX00327 PA 66 LNP* VERTON* RX00327 is a compound based on Nylon 66 resin containing proprietary fillers. Added feature of this material is: Structural. |