Polymer Property : Flexural Strength = 33.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	33.0 MPa	4780 psi	ASTM D790
Ravago Manufacturing Americas Hylon® N2000HL Nylon 6 (Cond) Information provided by Ravago.
Flexural Strength	33.0 MPa	4790 psi	ASTM D790
PolyOne Geon™ Vinyl Cellular E8202 Polyvinyl Chloride, Rigid (PVC, Rigid) All physicals were measured on an actual extruded part of a shutter profile.High rate inward foam applications.Density range .55-.70.Information provided by PolyOne
Flexural Strength	33.0 MPa	4790 psi	ISO 178
SABIC Innovative Plastics LNP COLORCOMP R1000 PA 66 LNP* COLORCOMP* R1000 is an unfilled Nylon 66.
Flexural Strength	33.0 MPa	4790 psi
Plastcom SLOVALEN PC 93 T 20 PP, 20% mineral filling, UV stabilization FeaturesModified PP for injection moulding with the content of 20 % mineral filling, uv stabilized. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased..
Flexural Strength	33.0 MPa	4790 psi	ASTM D790 A
Metabolix Mirelâ„¢ F1006 Injection Molding Grade PHA Bioplastic Mirel F1006 is FDA cleared for use in non-alcoholic food contact applications, from frozen food storage and microwave reheating to boiling water up to 212Â°F. FDA clearance includes products such..
Flexural Strength	33.0 MPa	4790 psi	ASTM D790 A
Metabolix Mirelâ„¢ P1004 Injection Molding Grade PHA Bioplastic Mirel P1004 is a general purpose injection molding grade with high toughness.About Mirel BioplasticsMirel is a family of bioplastic materials that have physical properties comparable to petroleum-ba..
Flexural Strength	33.0 MPa	4790 psi	ISO 178
Solvay TECHNYLÂ® eXten D 437P PA6.10 Description: TECHNYLÂ® eXten D 437P is a high viscosity, unfilled, plasticized, UV and heat stabilized PA6.10 for extrusion applications. TechnylÂ® eXten D 437P is a partially biosourced materia..
Flexural Strength	33.0 MPa	4790 psi	ASTM Test
Styrolution Styrolux 656C SBC Styrolux 656C is a high flow thermoplastic injection molding styrene-butadiene block copolymer. It has crystal clarity, good toughness, good stiffness, and warpage resistance for general molding ap..
Flexural Strength	33.0 MPa	4790 psi	ASTM D790
Styrolution StyroluxÂ® GH 58 SBC Description: StyroluxÂ® GH 58 is a high flow thermoplastic styrene-butadiene block copolymer with excellent mold release properties. It has crystal clarity, good toughness, good stiffness and warp..
Flexural Strength	33.0 MPa	4790 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp MH0200A PP (Europe-Africa-Middle East) LNP* Thermocomp* MH0200A is a compound based on Polypropylene resin containing High Specific Gravity Filler.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Strength	33.0 MPa	4790 psi	ISO 178
Unitika A1030FR PA6, Conditioned Information provided by Unitika Ltd.
Flexural Strength	33.0 MPa	4790 psi	ASTM D790
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman.
Flexural Strength	33.0 MPa	4790 psi	ASTM D790
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman.
Flexural Strength	33.0 MPa	4790 psi	ASTM D790
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman.
Flexural Strength	33.0 MPa	4790 psi	ASTM D790
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman.
Flexural Strength	33.0 MPa	4790 psi	ASTM D790
Entec Hypro™ PPC-CC20 Natural Copolymer Polypropylene, 20% Calcium Carbonate Filled Information provided by Entec
Flexural Strength	33.0 MPa	4790 psi	chs 0.05 in/min; ASTM D790
Diamond Polymers SBS 1001 Styrene Butadiene Block Copolymer Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Flexural Strength	33.0 MPa	4790 psi	2 mm/min; ISO 178
Eurostar Starpylen HU 70E3 HDPE, Injection Molding Starpylen HU 70E3 is a High Density Polypropylene Injection Molding Resin (also known as HU70E3)Information provided by Eurostar.
Flexural Strength	33.0 MPa	4790 psi	2 mm/min; ISO 178
Eurostar Starpylen MH0200A HDPE, Injection Molding Starpylen MH0200A is a High Density Polypropylene Injection Molding ResinInformation provided by Eurostar.
Flexural Strength	33.0 MPa	4790 psi	high temp bending
China-Yixing Longly Refractories Push Slab Corundum-Mullite Our company's production of a variety of corundum mullite push slab (moved plate), corundum-mullite seggar, corundum mullite corrugated board and other kinds of the kiln furniture, high refractorine..
Flexural Strength	33.0 MPa	4790 psi	ASTM D790
Aclo Accuguard Polypropylene CP1467V2CSL Copolymer Flame Retardant Copper Stabilized
Flexural Strength	33.0 MPa	4790 psi	ASTM D790
Aclo Accutech Polypropylene Copolymer CP0436T40L1 Talc Reinforced
Flexural Strength	33.0 MPa	4790 psi	ISO 178
Ascend Performance Materials Vydyne® 50BW Nylon 66, Dry as Molded Vydyne® 50BW is a general purpose Nylon 66 resin. Available in natural. Designed for extrusion applications that do not require use of a high-viscosity resin. This resin offers a well-balanced comb..
Flexural Strength	33.0 MPa	4790 psi	ASTM Test
BASF Styroclear GH 58 SBC Styroclear GH 58 is a high flow thermoplastic styrene-butadiene block copolymer with excellent mold release properties. It has crystal clarity, good toughness, good stiffness and warpage resistance..
Flexural Strength	33.0 MPa	4790 psi	ASTM D790
A. Schulman ComAlloy Voloy® 101 Polypropylene, Impact Modified, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	33.0 MPa @Thickness 19.0 mm	4790 psi @Thickness 0.750 in	ASTM D790
3A Composites Core Materials AIREX® PXw.385 Fiber-Reinforced Structural Foam Panel AIREX® PXw is a closed-cell, fiber reinforced polymer foam panel with a special formulation and very high mechanical properties. The sophisticated manufacturing process evenly distributes continuou..
Flexural Strength	33.0 MPa	4790 psi	ASTM D790
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman.
Flexural Strength	33.0 MPa	4790 psi	ISO 178
Ascend Performance Materials Vydyne® 50BWFS Nylon 66, Dry as Molded Vydyne® 50BWFS is a general purpose Nylon 66 resin. Available in natural. Designed for extrusion applications that do not require use of a highviscosity resin. This resin offers a well-balanced com..
Flexural Strength	33.0 MPa	4790 psi	2 mm/min; ISO 178
Sax Polymers SAXALEN PPC339T20 Polypropylene Copolymer, 20% Talc Filled SAXALEN PPC339T20 is a 20% mineral filled Polypropylene - Copolymer intended for injection molding with good flow properties und higher stiffness. The PP-Copolymer has low warpage behaviors and good..
Flexural Strength	33.0 MPa	4790 psi	ASTM D790
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman.