Polymer Property : Flexural Strength = 42.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	<= 42.0 MPa	<= 6090 psi	ISO 178
Polykemi AB POLYfill PPH K20040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
LG Chemical LUPOL GP-1000FA General Purpose Polypropylene, High Impact, Flame Retardant, Non-Bleed LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner..
Flexural Strength	42.0 MPa	6090 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP ML003S PP LNP* LUBRICOMP* ML003S is a compound based on Polypropylene resin containing 15% PTFE. Added features include: Heat Stabilized, Wear Resistant.
Flexural Strength	42.0 MPa	6090 psi
SPS Guang Zhou SAMATâ„¢ 5003 Flame-retarded Polypropylene Characteristic: Good chemical resistance, good mechanical properties, excellent long-term thermal stabilityApplications: E/E applianceInformation Provided by SPS (Guang Zhou) Ltd.
Flexural Strength	42.0 MPa	6090 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS (Asia Pacific) LNP THERMOCOMP* AH0230A is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: High Specific Gravity.
Flexural Strength	42.0 MPa	6090 psi	ISO 178
Styrolution PS 456EB HIPS Styrolution PS 456EB is a high flow, high impact polystyrene with a good heat resistance and a high stiffness, developed for injection blow molding applications, especially for bottle of yot.High fl..
Flexural Strength	42.0 MPa	6090 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP WX02869H Polyester, TP LNP THERMOCOMP* WX02869H is a compound based on Polyester, TP resin containing High Specific Gravity. Added features of this material include: High Impact.
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1908E is a 20% talc filled impact copolymer polypropylene product. Information provided by A. Schulman.
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1908E is a 20% talc filled impact copolymer polypropylene product. Information provided by A. Schulman.
Flexural Strength	42.0 MPa	6090 psi	ISO 178
Polyplastics Duracon® TD-25 Acetal Co-polymer (POM), High impact, Flexible DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1908E is a 20% talc filled impact copolymer polypropylene product. Information provided by A. Schulman.
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
Aclo Accuguard Polypropylene HP1362V2CSL Homopolymer Flame Retardant Copper Stabilized
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
Aclo Accutech Polypropylene Copolymer HP0334W20L Wollastonite Reinforced
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0334M30L Mica Reinforced
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0334M40L Mica Reinforced
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0336M20L Mica Reinforced
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0336W10L Wollastonite Reinforced
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0336W20L Wollastonite Reinforced
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0336W30L Wollastonite Reinforced
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0339W30L1 Wollastonite Reinforced
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0339W40L Wollastonite Reinforced
Flexural Strength	42.0 MPa	6090 psi	ISO 178
Azoty Tarnow™ TARNOFORM 500 HI4 POM Easy flow high impact grade, possessing also high damping capacityInformation provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Flexural Strength	42.0 MPa	6090 psi	ASTM Test
BASF Ultramid® 8202C HS PA6 (Conditioned) Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also..
Flexural Strength	42.0 MPa	6090 psi	ASTM Test
BASF Ultramid® 8202CQ PA6 (Conditioned) Ultramid 8202CQ is a low viscosity, PA6 injection molding homopolymer, possessing a modified crystalline structure or increased property performance and faster cycles. It is also available in pigme..
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
Aclo Accutech Polypropylene Copolymer HP0334W30L Wollastonite Reinforced
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
Aclo Accutech Polypropylene Copolymer HP0335W40L Wollastonite Reinforced
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0339M20L Mica Reinforced
Flexural Strength	42.0 MPa	6090 psi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0339W30L Wollastonite Reinforced
Flexural Strength	<= 42.0 MPa	<= 6090 psi	ISO 178
Polykemi AB POLYfill PPH TS15010 H VTUV1 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	42.0 MPa @Temperature 23.0 °C	6090 psi @Temperature 73.4 °F	2mm/min; 80x10x4mm; ISO 178
SYNTHOS Krasten® 336M High Impact Polystyrene Easy flow grade. Processed by injection moulding of intricate and thin-walled products that enables high production output.Synthos was formerly known as Kaucuk. All information provided by Synthos.