Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 655 MPa | 95000 psi | Transverse Rupture |
Pacific Sintered Materials F-241-T Iron Powdered Metal Applications:Low stressed mechanical componentsSoft magnetic applicationsEquivalent MPIF Specification: F-0000-20All information provided by Pacific Sintered Metals. |
|||
Flexural Strength | 655 MPa | 95000 psi | Transverse Rupture |
Pacific Sintered Materials FCC-216-P(HT) High Carbon Copper Steel Powdered Metal High strength, good impact resistant material for mechanical components. Excellent hardenability. High performance material with high strength and wear resistance after heat treatment.Equivalent MPI.. |
|||
Flexural Strength | 655 MPa | 95000 psi | Transverse Rupture |
PSM Industries Pacific Sintered Metals High Carbon Copper Steel FCC-216-P(HT) Powdered Metal High strength, Good impact resistant material for mechanical components, Excellent hardenability, High performance material with high strength and wear resistance after heat treatment Equivalent MP.. |
|||
Flexural Strength | 655 MPa | 95000 psi | Transverse Rupture |
PSM Industries Pacific Sintered Metals Iron F-241-T Powdered Metal Low stressed mechanical components, Soft magnetic applications Equivalent MPIF Specification: F-0000-20Information Provided by Pacific Sintered Metals, a division of PSM Industries |
|||
Flexural Strength | 655 MPa @Temperature 23.9 °C |
95000 psi @Temperature 75.0 °F |
Dry; ASTM D790 |
Park Electrochemical Nelcote® P-670F Polyester Prepreg, 7781 E-Glass Reinforced Nelcote® P-670F is a versatile, non-styrenated/low VOC polyester resin. P670F is used in a wide variety of applications including tooling and aircraft structures.Key Features and Benefits:Non-styre.. |
|||
Flexural Strength | 655 MPa @Temperature 22.0 °C |
95000 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
Menzolit Menzolit® HPC 1200 Unsaturated Polyester UP HPC 1200 is a special SMC for high strength applications. The glass level has been selected to combine mouldability with high strength and stiffness properties in orientation direction. The reinforc.. |