Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Yield Strength | 901 MPa | 131000 psi | Results normalized to 60% fibre volume for Carbon, 50% fibre volume for Kevlar; EFA TP-003 |
Hexcel® HexPly® 920CX-EP2015-47.5% 125°C Curing Epoxy Matrix Intermediate modulus, 6K carbon, 2x2 twill, 193 g/m2Information provided by HexCel |
|||
Compressive Yield Strength | 903 MPa @Temperature 23.0 °C |
131000 psi @Temperature 73.4 °F |
|
Hexcel® HexPly® 954-3 Curing Cyanate Resin, G80-600 Fiber Information provided by HexCel |
|||
Compressive Yield Strength | 904 MPa @Temperature 23.0 °C |
131000 psi @Temperature 73.4 °F |
prEN2580 Type A |
Hexcel® HexPly® M35-4 80-180°C Curing Epoxy Matrix, M35-4/40%/G1089/1000 Fabric Fiber: T800H 6K 2x2 Twill, 200 g/m2Information provided by HexCel |
|||
Compressive Yield Strength | 900 MPa | 131000 psi | 0.2%, Solution treated ~ 34 HRC |
Bohler-Uddeholm UDDEHOLM CORRAX® Precipitation Hardening Stainless Mold Steel A precipitation hardening stainless steel which offers excellent high corrosion resistance, excellent dimensional stability during hardening and good wear resistance. It can be used at its as-suppli.. |