Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Modulus | 2.60 GPa | 377 ksi | Type B, 5mm/min; ISO 604:2002 |
Nylacast Aquanyl Nylon 612 Copolymer Aquanyl is a copolymer of Nylon 6 and Nylon 12 produced via the anionic polymerization process using the monomer's Caprolactam and Laurinlactam. It has reduced water absorption, improved stability a.. |
|||
Compressive Modulus | 2.60 GPa | 377 ksi | Type B, 5mm/min; ISO 604:2002 |
Nylacast Cast Nylon 6, Glass Filled Information provided by Nylacast Ltd. |
|||
Compressive Modulus | 2.60 GPa | 377 ksi | Type B, 5mm/min; ISO 604:2002 |
Nylacast Nylube Cast Nylon 6, Lubricated (Blended Solid and Liquid Lubricant) This supreme wear resistant grade contains a combined liquid/solid lubricant system, which allows for a coefficient of friction as low as 0.08. The material has outstanding Pressure-Velocity capabil.. |
|||
Compressive Modulus | 2.60 GPa | 377 ksi | Type B, 5mm/min; ISO 604:2002 |
Nylacast POM C Acetal Copolymer The copolymer grade is the ideal combination of strength, stiffness and wears resistance. It absorbs very little moisture, is easily machinable and is genuinely porosity-free making it the preferred.. |
|||
Compressive Modulus | 2.60 GPa | 377 ksi | ISO 604 |
Polikim KESTLUB® Polyamide 6 + Lubricant Kestlub® is a special type of cast polyamide ideal for bearings. It is produced by adding lubricants to cast polyamide through special processes. It performs extremely well in bearing applications .. |
|||
Compressive Modulus | 2.60 GPa | 377 ksi | Sample Type A, 1 mm/min; ISO 604:2002 |
Global EPP PA 6C WFN Cast Polyamide 6 + Wax Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of .. |
|||
Compressive Modulus | 2.60 GPa | 377 ksi | Sample Type A, 1 mm/min; ISO 604:2002 |
Global EPP PA 6E Extruded Polyamide 6 Polyamides, commonly referred to as nylons, are macromolecular, partially crystalline thermoplastics. Their physical properties are mainly determined by the composition and structure of their molecu.. |
|||
Compressive Modulus | 2.60 GPa | 377 ksi | Sample Type A, 1 mm/min; ISO 604:2002 |
Global EPP POM C Acetal Copolymer Polyacetals are highly crystalline thermoplastics, characterised by their high mechanical strength, rigidity and impact resistance. Acetal absorbs very little moisture, enabling the product to maint.. |
|||
Compressive Modulus | 2.60 GPa | 377 ksi | ASTM D695 |
Saint-Gobain Meldin® 7001 CM Compression Molded Polyimide Meldin® 7001 CM unfilled polyimide base resin, compression moldedSpecification Qualifications:Satisfies Type I P for ASTM D 6456-99: Standard Specification for Finished Parts Made from Polyimide .. |
|||
Compressive Modulus | 2.60 GPa | 377 ksi | 23°C; ASTM D695 |
UBE UPIMOL® R Polyimide Shape Description: Ube's UPIMOL is an exceptionally heat-resistant polyimide Shape. This product has the same molecular structure as UPILEX, an ultra-high heat-resistant polyimide film developed by Ub.. |
|||
Compressive Modulus | 2.60 GPa | 377 ksi | DIN EN ISO 604 |
Wolf Kunststoff ZEDEX® ZX-530CD3 031 Polymer Alloy, Fiber Reinforced and PTFE Modified Main Characteristics: Dimensionally stable and rigid; Stress resistant; Extremely low wear to 100 ° CApplications: Chemical Engineering; Laboratory Technology; Automitve Technology; Machine ToolsIn.. |