Polymer Property : Compressive Modulus = 377 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Modulus	2.60 GPa	377 ksi	Type B, 5mm/min; ISO 604:2002
Nylacast Aquanyl Nylon 612 Copolymer Aquanyl is a copolymer of Nylon 6 and Nylon 12 produced via the anionic polymerization process using the monomer's Caprolactam and Laurinlactam. It has reduced water absorption, improved stability a..
Compressive Modulus	2.60 GPa	377 ksi	Type B, 5mm/min; ISO 604:2002
Nylacast Cast Nylon 6, Glass Filled Information provided by Nylacast Ltd.
Compressive Modulus	2.60 GPa	377 ksi	Type B, 5mm/min; ISO 604:2002
Nylacast Nylube Cast Nylon 6, Lubricated (Blended Solid and Liquid Lubricant) This supreme wear resistant grade contains a combined liquid/solid lubricant system, which allows for a coefficient of friction as low as 0.08. The material has outstanding Pressure-Velocity capabil..
Compressive Modulus	2.60 GPa	377 ksi	Type B, 5mm/min; ISO 604:2002
Nylacast POM C Acetal Copolymer The copolymer grade is the ideal combination of strength, stiffness and wears resistance. It absorbs very little moisture, is easily machinable and is genuinely porosity-free making it the preferred..
Compressive Modulus	2.60 GPa	377 ksi	ISO 604
Polikim KESTLUB® Polyamide 6 + Lubricant Kestlub® is a special type of cast polyamide ideal for bearings. It is produced by adding lubricants to cast polyamide through special processes. It performs extremely well in bearing applications ..
Compressive Modulus	2.60 GPa	377 ksi	Sample Type A, 1 mm/min; ISO 604:2002
Global EPP PA 6C WFN Cast Polyamide 6 + Wax Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of ..
Compressive Modulus	2.60 GPa	377 ksi	Sample Type A, 1 mm/min; ISO 604:2002
Global EPP PA 6E Extruded Polyamide 6 Polyamides, commonly referred to as nylons, are macromolecular, partially crystalline thermoplastics. Their physical properties are mainly determined by the composition and structure of their molecu..
Compressive Modulus	2.60 GPa	377 ksi	Sample Type A, 1 mm/min; ISO 604:2002
Global EPP POM C Acetal Copolymer Polyacetals are highly crystalline thermoplastics, characterised by their high mechanical strength, rigidity and impact resistance. Acetal absorbs very little moisture, enabling the product to maint..
Compressive Modulus	2.60 GPa	377 ksi	ASTM D695
Saint-Gobain MeldinÂ® 7001 CM Compression Molded Polyimide MeldinÂ® 7001 CM unfilled polyimide base resin, compression moldedSpecification Qualifications:Satisfies Type I P for ASTM D 6456-99: Standard Specification for Finished Parts Made from Polyimide ..
Compressive Modulus	2.60 GPa	377 ksi	23°C; ASTM D695
UBE UPIMOL® R Polyimide Shape Description: Ube's UPIMOL is an exceptionally heat-resistant polyimide Shape. This product has the same molecular structure as UPILEX, an ultra-high heat-resistant polyimide film developed by Ub..
Compressive Modulus	2.60 GPa	377 ksi	DIN EN ISO 604
Wolf Kunststoff ZEDEX® ZX-530CD3 031 Polymer Alloy, Fiber Reinforced and PTFE Modified Main Characteristics: Dimensionally stable and rigid; Stress resistant; Extremely low wear to 100 ° CApplications: Chemical Engineering; Laboratory Technology; Automitve Technology; Machine ToolsIn..