Mechanical Properties	Metric	English	Comments
Charpy Impact	20.0 J @Temperature 538 - 816 Â°C	14.8 ft-lb @Temperature 1000 - 1500 Â°F	Longitudinal
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Charpy Impact	20.0 J @Temperature 538 - 816 Â°C	14.8 ft-lb @Temperature 1000 - 1500 Â°F	Longitudinal
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, 12.7 mm (1/2 in.) thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Charpy Impact	20.0 J @Temperature 538 - 816 Â°C	14.8 ft-lb @Temperature 1000 - 1500 Â°F	Longitudinal
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, 15.9 mm thick bar Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Charpy Impact	20.0 J @Temperature 538 - 816 Â°C	14.8 ft-lb @Temperature 1000 - 1500 Â°F	Longitudinal
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 1.0 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Charpy Impact	20.0 J @Temperature 538 - 816 Â°C	14.8 ft-lb @Temperature 1000 - 1500 Â°F	Longitudinal
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 1.7 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Charpy Impact	20.0 J @Temperature 538 - 816 Â°C	14.8 ft-lb @Temperature 1000 - 1500 Â°F	Longitudinal
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 11.1 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Charpy Impact	20.0 J @Temperature 538 - 816 Â°C	14.8 ft-lb @Temperature 1000 - 1500 Â°F	Longitudinal
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 15.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Charpy Impact	20.0 J @Temperature 538 - 816 Â°C	14.8 ft-lb @Temperature 1000 - 1500 Â°F	Longitudinal
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816Â°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Charpy Impact	20.0 J @Temperature 538 - 816 Â°C	14.8 ft-lb @Temperature 1000 - 1500 Â°F	Longitudinal
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 4.8 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Charpy Impact	20.0 J @Temperature 538 - 816 Â°C	14.8 ft-lb @Temperature 1000 - 1500 Â°F	Longitudinal
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 7.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Charpy Impact	20.0 J @Temperature 538 - 816 Â°C	14.8 ft-lb @Temperature 1000 - 1500 Â°F	Longitudinal
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816Â°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Charpy Impact	20.0 J @Temperature 538 - 816 Â°C	14.8 ft-lb @Temperature 1000 - 1500 Â°F	Longitudinal
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, air cooled, 3.2 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Charpy Impact	20.0 J @Temperature -40.0 °C	14.8 ft-lb @Temperature -40.0 °F	Transverse
ThyssenKrupp XABO® 500 T Structural Steel This Material Specification applies to thermo mechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-..
Charpy Impact	20.0 J @Temperature -20.0 °C	14.8 ft-lb @Temperature -4.00 °F	Transverse
ThyssenKrupp XABO® 500 Structural Steel This Material Specification applies to thermo mechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-..
Charpy Impact	20.0 J @Temperature 538 - 816 °C	14.8 ft-lb @Temperature 1000 - 1500 °F	Longitudinal
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..