Polymer Property : Compressive Yield Strength = 5.00 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Yield Strength	0.0345 MPa @Strain 25.0 %	5.00 psi @Strain 25.0 %	Typical value, 0.2"/min. strain rate
Rogers Corporation Poron® 4701-30-20 Supported Urethane Foam, Very Soft, Supported with Clear Polyester Film Very soft, easily compressed for use where flexibility is a key requirement. Contains PET film reinforcement.Features and Benefits of PORON Products: Excellent compression set resistance which ena..
Compressive Yield Strength	0.0345 MPa @Strain 25.0 %	5.00 psi @Strain 25.0 %	Typical value, 0.2"/min. strain rate
Rogers Corporation Poron® 4701-30-20064 P Urethane Foam, Very Soft, Supported with Clear Polyester Film Very soft, easily compressed for use where flexibility is a key requirement. Contains PET film reinforcement. Standard available thickness 0.064"Features and Benefits of PORON Products: Excelle..
Compressive Yield Strength	0.0345 - 0.0827 MPa @Strain 25.0 %	5.00 - 12.0 psi @Strain 25.0 %	Range, 0.2"/min. strain rate
Rogers Corporation Poron® 4701-30-25 Urethane Foam, Very Soft Very soft, easily compressed for use where flexibility is a key requirement. Standard available thickness range from 0.021"Features and Benefits of PORON Products: Excellent compression set resi..
Compressive Yield Strength	0.0345 - 0.0827 MPa @Strain 25.0 %	5.00 - 12.0 psi @Strain 25.0 %	Range, 0.2"/min. strain rate
Rogers Corporation Poron® 4701-30-25037 P Urethane Foam, Very Soft, Supported with Clear Polyester Film Very soft, easily compressed for use where flexibility is a key requirement. Standard available thickness range from 0.021"Features and Benefits of PORON Products: Excellent compression set resi..
Compressive Yield Strength	0.0345 - 0.0827 MPa @Strain 25.0 %	5.00 - 12.0 psi @Strain 25.0 %	Range, 0.2"/min. strain rate
Rogers Corporation Poron® 4701-30-25047 P Urethane Foam, Very Soft, Supported with Clear Polyester Film Very soft, easily compressed for use where flexibility is a key requirement. Standard available thickness range from 0.021"Features and Benefits of PORON Products: Excellent compression set resi..
Compressive Yield Strength	0.0345 - 0.0758 MPa @Strain 25.0 %	5.00 - 11.0 psi @Strain 25.0 %	Range, 0.2"/min. strain rate
Rogers Corporation Poron® 4701-41-15 Urethane Foam, Soft, Enhanced Sealability Soft, enhanced sealability material offering greater closed-cell content for demanding vacuum sealing applications or low closure-force requirements. Standard available thickness range from 0.031"..
Compressive Yield Strength	0.0345 - 0.310 MPa @Strain 25.0 %	5.00 - 45.0 psi @Strain 25.0 %	Range, 0.2"/min. strain rate
Rogers Corporation Poron® 4701-50 Thin as Cast Urethane Foam, Firm, Thin as Cast Firm material used for managing high energy impact with gasketing needs. Standard available thickness range from 0.012" to 0.500" (0.30 mm to 12.7 mm).Features and Benefits of PORON Products: Exce..
Compressive Yield Strength	0.0345 - 0.0827 MPa @Strain 25.0 %	5.00 - 12.0 psi @Strain 25.0 %	Range, 0.2"/min. strain rate
Rogers Corporation Poron® 4701-30-25 Supported Urethane Foam, Very Soft, Supported with Clear Polyester Film Very soft, easily compressed for use where flexibility is a key requirement. Contains PET film reinforcement.Features and Benefits of PORON Products: Excellent compression set resistance which enab..