- Polymer Property : Tensile Strength at Break = 30.0 MPa
Polymer Property : Tensile Strength at Break = 30.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 MPa | 4350 psi | STN EN ISO 527-2 |
| Plastcom PLASTALEN® PH 91 SD Polypropylene Modified homopolymer PP for injection molding. General use in all industry branches. Delivered in natural mode and in the full RAL color scale.Information Provided by Plastcom spol. s r.o. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | |
| Plastcom SLOVALEN PC 13 T 30 PP, 30% mineral filling FeaturesModified copolymer PP for injection moulding or extrusion parts with the content of 30 % mineral filler. Increased rigidity, strength and impact strenght.Delivered in natural mode and in the.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycolac® GX3800F ABS High impact ABS for sheet extrusion and blow molding applications. FDA food contact compliant. |
|||
| Tensile Strength at Break | <= 30.0 MPa | <= 4350 psi | ISO/R527 |
| Polykemi AB POLYfill PP HIP16020FCF Polypropylene, Fast Cycle Information provided by Polykemi AB |
|||
| Tensile Strength at Break | <= 30.0 MPa | <= 4350 psi | ISO/R527 |
| Polykemi AB POLYfill PPH TS15020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 30.0 - 50.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
4350 - 7250 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 6012 PVDF homopolymer is a high-viscosity PVDF resin and is typically processed by extrusion or compression molding.Information provided by Solvay Specialty Polymers. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| 3M Dyneon™ PFA X 6505 UHP Perfluoroalkoxy Fluorothermoplastic
(discontinued **) Dyneon PFA X 6502 UPH, PFA X 6505 UHP and PFA X 6515 UHP are ultra-high purity fluorothermoplastics. These resins were developed for high-purity applications requiring ultra-low levels of metal and .. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | Extruded films: approx. 0.2 mm thickness; ISO 527 |
| Lubrizol Advanced Materials Pearlbond® D1160 Thermoplastic Polyurethane Pearlbond™ D1160 is a linear, aromatic polyurethane, supplied in form of small white granules, which combines a high crystallization rate and high thermoplasticity level. Applications: Pearlbo.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ISO 527 |
| Iran Petrochemical (PCC) I3 HC 7260(THE) High Density Polyethylene I3 (HC 7260) is a high density polyethylene with propylene as comonomer. The product has good impact strength, good stress cracking resistance, low warping and good flow ability as well as high dens.. |
|||
| Tensile Strength at Break | >= 30.0 MPa | >= 4350 psi | 50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Hyflon® MFA® F1520 Perfluoropolymer Hyflon® F is a family of MFA polymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, high flexural endurance, inherent flame resistance, low s.. |
|||
| Tensile Strength at Break | 30.0 - 50.0 MPa @Thickness 2.00 mm |
4350 - 7250 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Solef® 1006 Polyvinylidene Fluoride (PVDF) Solef® 1006 PVDF is a very low viscosity homopolymer resin mainly used in injection molding or in multifilament extrusion.Features: Homopolymer; Low ViscosityUses: General PurposeAdditional Prope.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | 50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Solef® 42308 Polyvinylidene Fluoride (PVDF) Solef® 42308 PVDF is specifically developed for coextrusion.Additional Properties: Crystallization Heat - ASTM D3418 51.6 J/g; Heat of Fusion - ASTM D3418 52.7 J/gInformation provided by Solvay S.. |
|||
| Tensile Strength at Break | 30.0 - 50.0 MPa @Thickness 2.00 mm |
4350 - 7250 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF) Solef® 6012 PVDF homopolymer is a high-viscosity PVDF resin and is typically processed by extrusion or compression molding.Features: High Viscosity; HomopolymerAdditional Properties: Crystallizat.. |
|||
| Tensile Strength at Break | >= 30.0 MPa | >= 4350 psi | 50mm/min; ASTM D638 |
| Shanghai Ofluorine J-2 PVDF Extrusion Grade Description: J-2 PVDF is a kind of granules homopolymer, which has middle melt viscosity, J-2 is more suitable for extrusion process. J-2 PVDF pellets as raw materials, the finished products has exc.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| SCG Chemicals EL-Leneâ„¢ H6007JU High Density Polyethylene Injection Molding Key Characteristics:Good processabilityHigh rigidityHigh impact resistanceGood weathering resistance (UV stabilizer)Recommended Applications:Crates for soft drink, bottles, pallet, garbage bins, con.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D412 |
| Lubrizol STAT-RITE® E-1140 Ester-Type Static Dissipative Polymer Description: Stat-Rite® E-1140 is a static dissipative thermoplastic polyurethane (TPU) alloy. Stat-Rite E-1140 utilizes the patented Stat-Rite inherently dissipative polymer (IDP) alloy system to .. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| A. Schulman POLYFORT™ FPP 4020 20% Mineral-Filled Polypropylene DescriptionPolyfort® FPP 4020 is a 20% mineral-filled polypropylene designed for use when improved heat resistance and high stiffness is needed.Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| A. Schulman POLYFORT™ FPP 4020 20% Mineral-Filled Polypropylene DescriptionPolyfort® FPP 4020 is a 20% mineral-filled polypropylene designed for use when improved heat resistance and high stiffness is needed.Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | conditioned; ISO 527-1/-2 |
| EMS-Grivory Grivory® XE 4128 black 9221 PA610 Product description: Grilamid XE 4128 black 9221 is a modified high viscosity Polyamide 610 for extrusion as well as injection molding. A characteristic of tubes made out of this material is the hig.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | 50 mm/min; ISO 527 |
| Chi Mei Polylac® PA-764B ABS - Flame Retardant F.R. Weather Resistant |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ISO 527-1/-2 |
| DuPont Performance Polymers Hytrel® HTR8685 BK022A Polyester Elastomer TPC-ET
(Unverified Data**) 44 Shore D Lubricated High Viscosity Polyester Elastomer with Superior Fatigue Resistance Developed for Blow Molding Hytrel HTR8685 BK022A is designed for blow molding or processing techniques requi.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0339T30L1 Talc Reinforced |
|||
| Tensile Strength at Break | >= 30.0 MPa | >= 4350 psi | ASTM D638 |
| Braskem UTEC® 5040 Ultra High Molecular Weight Polyethylene Applications which require high wear resistance - technical parts, RAM extruded and compression molded sheets, rods and profiles.Information provided by Braskem. |
|||
| Tensile Strength at Break | 30.0 MPa @Temperature 80.0 °C |
4350 psi @Temperature 176 °F |
ISO Data |
| BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Conditioned) Ultramid 8231G HS BK-102 is a black pigmented heat stabilized, 14% glass fiber reinforced PA6 injection molding compound.The glass fiber reinforcement enhances performance such as strength, stiffnes.. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Aclo Accucomp ABS ABS809SL Extrusion Grade |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| 3M Dyneon™ PFA 6515 UHPZ Perfluoroalkoxy Fluorothermoplastic Granules Dyneon PFA X 6502 UPH, PFA X 6505 UHP and PFA X 6515 UHP are a new series of ultra-high purity fluorothermoplastics. These resins were developed for high-purity applications requiring ultra-low leve.. |
|||
| Tensile Strength at Break | 30.0 - 50.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
4350 - 7250 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Solef® 9009 Polyvinylidene Fluoride (PVDF)
(discontinued **) Solef® 9009 PVDF homopolymer has low/medium viscosity and is used in film extrusion and injection molding.Information provided by Solvay Specialty Polymers. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | |
| UBE UBEPOL BR15HB HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBEPOL-BR15HB is characterized by the highest branching of these 3 grades and is adapted by many PS manufacturers.Information provided by UBE. |
|||
| Tensile Strength at Break | 30.0 MPa | 4350 psi | STN EN ISO 527-2 |
| Plastcom SLOVALEN PH 91 N Polypropylene Homopolymer FeaturesModified homopolymer PP for injection moulding. General use in all industry branches - packing material, garden flower-pots, toys, furniture industry, hinges, fasteners, clamps, office chai.. |
|||
| Tensile Strength at Break | <= 30.0 MPa | <= 4350 psi | ISO/R527 |
| Polykemi AB POLYfill PPH T5038 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||