- Polymer Property : Tensile Strength at Break = 11900 psi
Polymer Property : Tensile Strength at Break = 11900 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ASTM D638 |
| Niche Polymer PPCG40BK Copolymer PP, 40% Glass Fiber Filled Information provided by Niche Polymer |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI (Europe-Africa-Middle East) LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp KFL22 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KFL22 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP f.. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics ULTEM 1285 PEI Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact Compliant in recognized colors. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics ULTEM 4000 PEI Glass fiber, PTFE, and Graphite filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 listing. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics ULTEM 4000 PEI (Asia Pacific) Glass fiber, PTFE, and Graphite filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 listing. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Ultem HFATX200 PEI+PCE (Asia Pacific) High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Ultem HFATX200 PEI+PCE (Europe-Africa-Middle East) High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 4012 PBT (Europe-Africa-Middle East) VALOX 4012 is a 10% high strength glass fibre reinforced PBT injection moulding resin with improved mechanical properties. Applications: connectors. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 732E PBT + PC + PET 30% glass/mineral reinforced, excellent thermal performance, low shrinkage and warp. Easy flow. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® K4530 PBT (Europe-Africa-Middle East) 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP AF006 ABS (Europe-Africa-Middle East) LNP* Thermocomp* AF006 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP AF006XXZ ABS (Europe-Africa-Middle East) LNP* Thermocomp* AF006XXZ is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Thermocomp RFZ71S PA 66 LNP* Thermocomp* RFZ71S is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for t.. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON AE002 ABS LNP* STAT-KON* AE002 is a compound based on ABS resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | DIN EN ISO 527 |
| Wolf Kunststoff ZEDEX® ZX-410 A4A Polymer Alloy ZX-410 is a bearing material with excellent properties and a very affordable price.Main Characteristics: Hard, Stiff, Tough; High dimensional stability; High chemical resistance; High water resistan.. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ISO 527 |
| Ecomass® 4301TU74 Tungsten Filled Polyphthalamide Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applicationsTungsten Powder Filled Polyphthalamide (PPA)Very Good ToughnessInformation provided by Technical Polymers |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | 5 mm/min; ISO 527 |
| CP-Polymer-Technik Wellamid® 6000 GS 40 HWCP 40% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | 50%RH; ISO 527-1/-2 |
| DuPont Performance Polymers Minlon® 22C NC010 Nylon 66
(Unverified Data**) 38% Mineral/Glass Reinforced Polyamide 66 Minlon 22C NC010 is a 38% mineral/glass reinforced heat stabilized polyamide 66 resin for injection molding.Information provided by DuPont Performance Polym.. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ISO 527-1/-2 |
| DuPont Performance Polymers Rynite® 935 BK505 Polyethylene Terephthalate (PET)
(Unverified Data**) 35% Glass Reinforced Polyethylene Terephthalate Rynite 935 BK505 is a 35% mica/glass reinforced modified polyethylene terephthalate resin with exceptionally low warpage excellent electrical properti.. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | DAM; ISO 527-1/-2 |
| DuPont Performance Polymers Minlon® 73M30 NC010 Nylon 6
(Unverified Data**) 30% Mineral Reinforced Polyamide 6 Minlon 73M30 NC010 is a 30% mineral reinforced heat stabilized polyamide 6 resin for injection molding. It has isotropic properties and low warpage.Information pro.. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ISO 527 |
| Eurostar Starflam PZ0052E PA6, 25% Glass Filled, Injection Molded PZ0052E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding (also known as PF1005Z222 or PA625GFUZ22)Information provided by Polymer Technolo.. |
|||
| Tensile Strength at Break | 82.0 MPa @Temperature 80.0 °C |
11900 psi @Temperature 176 °F |
ASTM Test |
| BASF Petra® 330 FR BK-112 30% Glass Filled PET Petra 330 FR BK-112 is a 30% glass reinforced, flame retardant PET, pigmented black injection molding compound rated UL94 V-0 in a 1/64 inch thickness. The product is designed for injection molding.. |
|||
| Tensile Strength at Break | 82.0 MPa @Temperature 80.0 °C |
11900 psi @Temperature 176 °F |
ISO Data |
| BASF Petra® 330 FR BK-112 30% Glass Filled PET Petra 330 FR BK-112 is a 30% glass reinforced, flame retardant PET, pigmented black injection molding compound rated UL94 V-0 in a 1/64 inch thickness. The product is designed for injection molding.. |
|||
| Tensile Strength at Break | 82.0 MPa | 11900 psi | ISO R 527 |
| Addiplast Addilene H 511 V30 Polypropylene Homopolymer Glass fiber reinforced, high modulus and improved stiffnessInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 82.0 MPa @Temperature 23.0 °C |
11900 psi @Temperature 73.4 °F |
DAM; ISO 527 |
| DuPont Performance Polymers Zytel® 70GB30HSL NC010 Nylon 66 Zytel® 70GB30HSL NC010 is a 30% glass bead reinforced heat stabilized polyamide 66 resin.Information provided by DuPont Performance Polymers |
|||