Polymer Property : Tensile Strength at Break = 13.9 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	13.9 MPa	2020 psi
NEU NeuSoft™ 597-50A Industrial Ether TPU / SBC blend
Tensile Strength at Break	13.9 MPa	2020 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible XV3796 Polyvinyl Chloride, Flexible (PVC, Flexible) All ingredients used in the formulation of this compound are listed in the United States FDA Code of Federal Regulations, Title 21. The only restriction is that the plasticizer is For foods of high ..
Tensile Strength at Break	13.9 MPa @Temperature 200 Â°C, Time 360000 sec	2010 psi @Temperature 392 Â°F, Time 100 hour	After Dry Heat Aging; ASTM D865
Seals Eastern 7130 Fluorocarbon-Elastomer FKM specially for oil & gas service.Information provided by Seals Eastern, Inc.
Tensile Strength at Break	13.9 MPa	2020 psi
Daikin DAI-EL G-716 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Features: Minimal compression set and fast vulcanization.Information provided by..
Tensile Strength at Break	13.9 MPa	2020 psi	Across Flow; ASTM D412
ExxonMobil Santoprene® 251-92W232 Thermoplastic Elastomer A hard, colorable, flame retardant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material has good fluid resistance and contains non-ether brominated flame retard..
Tensile Strength at Break	13.9 MPa	2010 psi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FC 2110Q Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2110Q can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu..