Daikin DAI-EL G-716 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Daikin Industries
Trade Name DAI-EL
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Daikin DAI-EL G-716 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Features: Minimal compression set and fast vulcanization.Information provided by Daikin Industries.
Physical Properties Metric English Comments
Specific Gravity 1.85 g/cc
1.85 g/cc
at 25°C
Mooney Viscosity 40

@Temperature 121 °C
40

@Temperature 250 °F
ML 1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 72
72
Peak value, at 25°C
Tensile Strength at Break 13.9 MPa
2020 psi
Tensile Strength, Yield 4.50 MPa

@Strain 100 %
653 psi

@Strain 100 %
Elongation at Break 210 %
210 %
Tear Strength 24.5 kN/m
140 pli
at 25°C
Compression Set 7.0 %
7.0 %
70 hours at 25°C
5.0 %

@Temperature 100 °C
5.0 %

@Temperature 212 °F
70 hours
8.0 %

@Temperature 175 °C
8.0 %

@Temperature 347 °F
70 hours
13 %

@Temperature 200 °C
13 %

@Temperature 392 °F
70 hours
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -18.0 °C
-0.400 °F
TR test, TR10
-14.5 °C
5.90 °F
Gehman torsion test, T10
-10.0 °C
14.0 °F
TR test, TR70
-6.50 °C
20.3 °F
Gehman torsion test, T2
Brittleness Temperature -18.0 °C
-0.400 °F
Processing Properties Metric English Comments
Processing Temperature 170 °C
338 °F
Cure Measuring Temperature
Cure Time 3.20 min
0.0533 hour
Curelastmeter