Polymer Property : Tensile Strength at Break = 17200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	119 MPa	17200 psi	ASTM D638
A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman.
Tensile Strength at Break	119 MPa	17200 psi	ASTM D638
A. Schulman VOLOY™ 461 Glass Reinforced, Flame Retardant PBT Alloy Information provided by A. Schulman.
Tensile Strength at Break	119 MPa	17200 psi	ASTM D638
A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman.
Tensile Strength at Break	119 MPa	17200 psi	ASTM D638
A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman.
Tensile Strength at Break	119 MPa	17200 psi	ASTM D638
A. Schulman VOLOY™ 461 Glass Reinforced, Flame Retardant PBT Alloy Information provided by A. Schulman.
Tensile Strength at Break	119 MPa	17200 psi	ASTM D638
A. Schulman VOLOY™ 461 Glass Reinforced, Flame Retardant PBT Alloy Information provided by A. Schulman.
Tensile Strength at Break	119 MPa	17200 psi	ASTM D638
A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman.
Tensile Strength at Break	119 MPa	17200 psi	ASTM D638
A. Schulman VOLOY™ 461 Glass Reinforced, Flame Retardant PBT Alloy Information provided by A. Schulman.
Tensile Strength at Break	119 MPa	17200 psi	ASTM D638
A. Schulman VOLOY™ 461 Glass Reinforced, Flame Retardant PBT Alloy Information provided by A. Schulman.
Tensile Strength at Break	119 MPa	17200 psi	ASTM D638
A. Schulman VOLOY™ 461 Glass Reinforced, Flame Retardant PBT Alloy Information provided by A. Schulman.
Tensile Strength at Break	119 MPa	17200 psi	ASTM D638
A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman.
Tensile Strength at Break	119 MPa	17200 psi	ASTM D638
A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman.