Polymer Property : Tensile Strength at Break = 19.3 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	19.3 MPa	2800 psi	2 in/min; ASTM D638
RheTech Products FT1002-00A Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	19.3 MPa	2800 psi	2 in/min; ASTM D638
RheTech Products FT1003-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Step and hitch padsInterior component and trimA/B pillarsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	19.3 MPa	2800 psi	2 in/min; ASTM D638
RheTech Products FT4650-01UV Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Scuff platesExterior grillesBodyside moldingsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	19.3 MPa	2800 psi	2 in/min; ASTM D638
RheTech Products FT4650-583UV Thermoplastic Polyolefin, UV Stabilized, Exterior DX9 Black Applications: Scuff platesExterior grillesBodyside moldingsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	19.3 MPa	2800 psi	2 in/min; ASTM D638
RheTech Products FT4702-527UV Thermoplastic Polyolefin, UV Stabilized, XS9 Dark Neutral Metallic Applications: Exterior door moldingsRigid bumper coversBodyside claddings and fairingsAutomotive grillesInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	19.3 MPa	2800 psi	2 in/min; ASTM D638
RheTech Products FT4702-715UV Thermoplastic Polyolefin, UV Stabilized, ZSP Deep Grey Applications: Exterior componentsGrillesBumper trimDoor componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	19.3 MPa	2800 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Elastamax™ HTE 3080 Polyvinyl Chloride + NBR (PVC+NBR) Elastamax™ HTE Series thermoplastic elastomers (TPEs) are based upon compounded blends of PVC resins and nitrile rubber. These elastomeric materials provide outstanding resistance to hydrocarbons a..
Tensile Strength at Break	19.3 MPa	2800 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible R4294W Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength at Break	19.3 MPa	2800 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible R4294Y Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength at Break	19.3 MPa	2800 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible XV3793 Polyvinyl Chloride, Flexible (PVC, Flexible) All ingredients used in the formulation of this compound are listed in the United States FDA Code of Federal Regulations, Title 21. The only restriction is that the plasticizer is For foods of high ..
Tensile Strength at Break	19.3 MPa	2800 psi	ASTM D4745
3M Dyneon™ CC503 Custom Fluoropolymer Compound (discontinued **) This compound consists of a mixture of 15% mineral blended with PTFE.Information provided by Dyneon, A 3M Company
Tensile Strength at Break	19.3 MPa	2800 psi	510 mm/min; ASTM D412A
PolyOne Elastamax™ XL 0131-61 Styrene Butadiene Block Copolymer (SBC) (discontinued **) A thermoplastic elastomer compound formulated for use in food contact applications. The physical properties listed above are typical values obtained on laboratory prepared samples and tested in acco..
Tensile Strength at Break	19.3 MPa	2800 psi	ASTM D412
ITW Devcon FlexaneÂ® Rubber Repair / Castable Urethane 94 Liquid, Black Information provided by ITW Devcon
Tensile Strength at Break	>= 19.3 MPa	>= 2800 psi	ASTM D412 Method A
Seals Eastern 7182X Fluorocarbon-Elastomer Formulated AFLASÂ®. Ultra-low compressive stress relaxation for alkaline, high-temperature service.Information provided by Seals Eastern, Inc.
Tensile Strength at Break	19.3 MPa	2800 psi	ASTM D638
Teknor Apex APEXÂ® 3800-85 Polyvinyl Chloride, Flexible Features: DEHP Plasticizer; Ethylene Oxide Sterilizable; High Heat Resistance Uses: Medical/Healthcare Applications Processing Method: Injection Molding Forms: PelletsInformation Provided by Teknor ..
Tensile Strength at Break	19.3 MPa	2800 psi	ASTM D638
Teknor Apex APEXÂ® 65006 Polyvinyl Chloride, Flexible Notes: 75Â°C Jacket; RoHS Compliant Uses: Wire and Cable ApplicationsForms: PelletsInformation Provided by Teknor Apex
Tensile Strength at Break	19.3 MPa	2800 psi	ASTM D638
Teknor Apex APEXÂ® 84856 Polyvinyl Chloride, Flexible Notes: 90Â°C Insulation; RoHS Compliant Features: Flame Retardant; Sunlight Resistant (720 hours) Uses: Cable JacketingAgency Ratings: UL 62; UL QMTT2 .E73402 Forms: Pellets Wire Types: SJTW; STWI..
Tensile Strength at Break	19.3 MPa	2800 psi	ASTM D638
A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010HF-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristic..
Tensile Strength at Break	19.3 MPa	2800 psi	ASTM D638
A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010HF-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristic..
Tensile Strength at Break	19.3 MPa	2800 psi	vs. aluminum; 60 s set time
Elmer's Products Aron Alpha® 212E Cyanoacrylate Adhesive (Industrial Krazy Glue™) For clean, fast applications. Best for high speed automated assembly.Medium gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on metal substrates. Excellent on porous s..
Tensile Strength at Break	19.3 MPa	2800 psi	vs. aluminum; 3 s set time
Elmer's Products Aron Alpha® 221F Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break	19.3 MPa	2800 psi	vs. aluminum; 15 s set time
Elmer's Products Aron Alpha® 241F Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break	19.3 MPa	2800 psi	vs. aluminum; 15 s set time
Elmer's Products Aron Alpha® 253TX Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break	19.3 MPa	2800 psi	vs. aluminum; 60 s set time
Elmer's Products Aron Alpha® 241E Cyanoacrylate Adhesive (Industrial Krazy Glue™) For clean, fast applications. Best for high speed automated assembly.Low gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on metal substrates. Excellent on porous subs..
Tensile Strength at Break	19.3 MPa	2800 psi	vs. aluminum; 10 s set time
Elmer's Products Aron Alpha® 252F Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on..
Tensile Strength at Break	19.3 MPa	2800 psi	ASTM D3574
3M 471 Vinyl Tape 3M™ Vinyl Tape 471 is a conformable colored (9 colors plus transparent) tapes made from vinyl backing with rubber adhesive. They are ideal for many lane and safety markings, color coding, abrasion ..
Tensile Strength at Break	19.3 MPa	2800 psi	ASTM D3574
3M 4712 Vinyl Tape 3M™ Vinyl Tape 4712 is a conformable colored (9 colors plus transparent) tapes made from vinyl backing with rubber adhesive. They are ideal for many lane and safety markings, color coding, abrasion..
Tensile Strength at Break	19.3 MPa	2800 psi	ASTM D638
Teknor Apex APEX® 1013 Polyvinyl Chloride, Semi-Rigid Notes: 60°C General Purpose; RoHS Compliant Uses: Connectors; Grommets; Plugs; Strain ReliefsForms: Pellets Processing Method: Injection Molding Agency Ratings: UL QMFZ2 .E54709 Wire Types: Molded ..
Tensile Strength at Break	19.3 MPa	2800 psi	ASTM D638 ISO 527-2
DuPont Elvax® 4355 Ethylene Vinyl Acetate (discontinued **) DuPont™ Elvax® 4355 is an ethylene-vinyl acetate / acid terpolymer resin for use in industrial applications.ApplicationsElvax® 4355 resins can be used for the following applications: adhesives, s..