- Polymer Property : Tensile Strength at Break = 23.1 MPa
Polymer Property : Tensile Strength at Break = 23.1 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 23.1 MPa | 3350 psi | Type IV, 510 mm/min; ASTM D638 |
| PolyOne Geon™ Vinyl Flexible R279AE Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
| Tensile Strength at Break | 23.1 MPa | 3350 psi | ASTM D638 |
| Teknor Apex APEX® 3600-90NT Polyvinyl Chloride, Flexible Uses: Medical/Healthcare Applications Agency Ratings: NSF 61 Forms: Pellets Additional Information: First Generation SeriesInformation Provided by Teknor Apex |
|||
| Tensile Strength at Break | 23.1 MPa | 3350 psi | ASTM D638 |
| Teknor Apex APEX® 3700-90 Polyvinyl Chloride, Flexible Features: DEHP Plasticizer; Ethylene Oxide Sterilizable; High Heat Resistance Uses: Medical/Healthcare Applications Processing Method: Extrusion Forms: PelletsInformation Provided by Teknor Apex |
|||
| Tensile Strength at Break | 23.1 MPa | 3350 psi | ASTM D638 |
| Teknor Apex APEX® 65001 Polyvinyl Chloride, Flexible Notes: RoHS Compliant Features: Flame Retardant; Non-lead Uses: Communication Wire Jacketing Wire Types: CL2; CL3; CM; FPL; MP; OFN Agency Ratings: NEC Article 725; NEC Article 760; NEC Article 770;.. |
|||
| Tensile Strength at Break | 23.1 MPa | 3350 psi | ASTM D638 |
| Teknor Apex APEX® 90-A471R-90-NT Polyvinyl Chloride, Flexible Features: DEHP Plasticizer; Radiation (Gamma) Resistant; Radiation Sterilizable Uses: Medical/Healthcare Applications; Tubing Processing Method: Extrusion Forms: PelletsInformation Provided by Tekno.. |
|||
| Tensile Strength at Break | 23.1 MPa | 3350 psi | ASTM D638 |
| Teknor Apex APEX® 65001 FOB Polyvinyl Chloride, Flexible Notes: RoHS Compliant Forms: PelletsInformation Provided by Teknor Apex |
|||
| Tensile Strength at Break | 23.1 MPa | 3350 psi | ASTM D1708 |
| GEHR Plastics ECOGEHR® WPC-30PE Composite of 70% Wood Fibers and 30% Polyethylene (PE)
(discontinued **) Wood-polymer-composites (WPC) - these materials are composites of standard polymers and wood fibers. The excellent binding of the wood fibers to the polymer gives the materials extremely high mecha.. |
|||
| Tensile Strength at Break | 23.1 MPa | 3350 psi | ASTM D4745 |
| 3M Dyneon™ CC103 Custom Fluoropolymer Compound
(discontinued **) This compound consists of a mixture of 15% fiberglass blended with PTFE.Information provided by Dyneon, A 3M Company |
|||