Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 276 - 345 MPa | 40000 - 50000 psi | Brass butt joint |
Lucas-Milhaupt BRAZE 450 Silver Based Cadmium Free Filler Metal Characteristics:Braze 450 is an intermediate temperature cadmium free silver brazing filler metal with sufficient melting range (145EF) to properly braze joints with the range of fits encountered in.. |
|||
Tensile Strength at Break | 276 - 345 MPa | 40000 - 50000 psi | Nickel-Silver butt joint |
Lucas-Milhaupt BRAZE 700 (Medium) Silver Based Cadmium Free Filler Metal Characteristics: This alloy is a intermediate silver brazing filler metals with a slight tendency to liquate (i.e. separate into low and high melting constituents) if heated slowly through their mel.. |
|||
Tensile Strength at Break | 276 - 345 MPa | 40000 - 50000 psi | Low Carbon Steel butt joint |
Lucas-Milhaupt BRAZE 560 Characteristics:Braze 560 is a low temperature, free-flowing brazing filler metal with a slight tendency to liquate (i.e. separate into low and high melting constituents) if heated slowly through it.. |
|||
Tensile Strength at Break | 276 - 345 MPa | 40000 - 50000 psi | Nickel-Silver butt joint |
Lucas-Milhaupt BRAZE 750 (Hard) Silver Based Cadmium Free Filler Metal Characteristics: This alloy is a intermediate silver brazing filler metals with a slight tendency to liquate (i.e. separate into low and high melting constituents) if heated slowly through their mel.. |
|||
Tensile Strength at Break | 276 MPa | 40000 psi | ASTM D638 |
Techmer ES Electrafil® J-1/CF/40 BK PA66 |
|||
Tensile Strength at Break | 276 MPa | 40000 psi | ASTM D638 |
Techmer ES Electrafil® J-1/CF/40 NAT PA66 |
|||
Tensile Strength at Break | 276 MPa | 40000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP VERTON RV00AES PA 66 (Europe-Africa-Middle East) LNP VERTON* RV00AES is a compound based on PA 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. |
|||
Tensile Strength at Break | 276 MPa | 40000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Verton RV00AESM PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00AESM is a compound based on PA66 resin containing Long Glass Fiber. Added features include: Easy Moldin, Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Mid.. |
|||
Tensile Strength at Break | 276 MPa | 40000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP VERTON RV00AESP PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00AESP is a compound based on PA66 resin containing Long Glass Fiber. Added features include : Easy Molding, Heat Stabilized. |
|||
Tensile Strength at Break | 276 MPa | 40000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP VERTON RV00AESS PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00AESS is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Easy Molding, Heat Stabilized. |
|||
Tensile Strength at Break | 276 MPa | 40000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP VERTON RV00AEU PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00AEU is a compound based on PA 66 resin containing Long Glass Fiber. Added features include : Easy Molding, UV Stabilized. |
|||
Tensile Strength at Break | 276 MPa | 40000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP VERTON RV00AEX5 PA6.6 (Europe-Africa-Middle East) LNP* VERTON* Is a compound based on PA66 resin containing Long Glass Fiber. Added features include: Easy Molding, Heat Stabilized. |
|||
Tensile Strength at Break | 276 MPa | 40000 psi | Longitudinal direction; ISO 527 |
Azdel Plus U421-B01 42% Directionalized Continuous Fiber Mat / PP Resin Matrix AZDEL® U421-B01 is a glass mat thermoplastic laminate based upon a combination of random oriented continuous fiber mat and oriented fiber mat contained within a polypropylene resin matrix. This co.. |
|||
Tensile Strength at Break | >= 276 MPa | >= 40000 psi | |
Carlson 90 10 Cu Ni Copper-Nickel Alloy General DescriptionCarlson Alloy 90 10 Cu Ni is a copper-based alloy developed as a cost-effective substitute for 70 30 Cu Ni. An addition of approximately 1.4% iron was made to increase its resist.. |