Lucas-Milhaupt BRAZE 560

Category Metal , Nonferrous Metal , Precious Metal , Silver Alloy , Solder/Braze Alloy
Manufacturer Lucas-Milhaupt
Trade Name BRAZE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lucas-Milhaupt BRAZE 560.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics:Braze 560 is a low temperature, free-flowing brazing filler metal with a slight tendency to liquate (i.e. separate into low and high melting constituents) if heated slowly through its melting range. Applications:Braze 560 is a silver-based brazing alloy used for ferrous and non-ferrous alloys in joints requiring a low temperature, cadmium-free alloy, as in food handling equipment. For improved corrosion resistance in joints on stainless steel, use alloys containing small amounts of nickel, such as Braze 630 or Braze 505. Specifications:This alloy conforms to the following specifications-AWS A5.8 BAg-7, ASME Boiler & Pressure Vessel Code Sec. II C SFA-5.8 BAg-7, SAE AMS 4763 Information provided by Lucas-Milhaupt, Inc.
Physical Properties Metric English Comments
Density 9.42 g/cc
0.340 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength at Break 172 - 207 MPa
25000 - 30000 psi
Copper butt joint
207 - 276 MPa
30000 - 40000 psi
Brass butt joint
276 - 345 MPa
40000 - 50000 psi
Low Carbon Steel butt joint
Thermal Properties Metric English Comments
Melting Point 618.3 - 651.7 °C
1145 - 1205 °F
Solidus 618.3 °C
1145 °F
Melting Point
Liquidus 651.7 °C
1205 °F
Flow Point
Component Elements Properties Metric English Comments
Copper, Cu 21 - 23 %
21 - 23 %
Other, total <= 0.15 %
<= 0.15 %
Silver, Ag 55 - 57 %
55 - 57 %
Tin, Sn 4.5 - 5.5 %
4.5 - 5.5 %
Zinc, Zn 15 - 19 %
15 - 19 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00002075 ohm-cm
0.00002075 ohm-cm
Descriptive Properties Value Comments
Color White