Polymer Property : Tensile Strength at Break = 29300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	202 MPa	29300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP IF00C PA6.12 LNP* THERMOCOMP* IF00C is a compound based on Nylon 6/12 resin containing 60% Glass Fiber.
Tensile Strength at Break	202 MPa	29300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RX00713H PA 66 LNP* Thermocomp* RX00713H is a compound based on Nylon 6/6 containing proprietary fillers. Characteristics of this grade are: Healthcare.
Tensile Strength at Break	202 MPa	29300 psi	ASTM D638
SABIC Innovative Plastics LNP VERTON RX89047 PA 66 LNP* VERTON* RX89047 is a compound based on Nylon 66 resin containing Proprietary Fillers. Added feature of this grade is: Structural.
Tensile Strength at Break	202 MPa	29300 psi	ASTM D638
SABIC Innovative Plastics LNP VERTON RX89047 PA 66 (Asia Pacific) LNP* Verton* RX89047 is a compound based on Nylon 66 resin.
Tensile Strength at Break	202 MPa	29300 psi	ASTM D638
SABIC Innovative Plastics LNP VERTON RX89047 PA 66 (Europe-Africa-Middle East) LNP* Verton* RX89047 is a compound based on Nylon 66 resin.