Polymer Property : Tensile Strength at Break = 34200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	236 MPa	34200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RCL26 PA6.6 LNP* LUBRICOMP* RCL26 is a compound based on Nylon 66 containing 30% Carbon Fiber, 10% PTFE. Added features of this grade include: Wear Resistant, Electrically Conductive.
Tensile Strength at Break	236 MPa	34200 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP UF008H PPA LNP THERMOCOMP* UF008H is a compound based on Polyphthalamide resin containing 40% Glass Fiber. Added feature of this grade is: Healthcare.
Tensile Strength at Break	236 MPa	34200 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP QC006 PA 6/10 (Asia Pacific) LNP* THERMOCOMP* QC006 is a compound based on Nylon 6/10 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Tensile Strength at Break	236 MPa	34200 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP UF008H PPA (Asia Pacific) LNP THERMOCOMP* UF008H is a compound based on Polyphthalamide resin containing Glass Fiber.
Tensile Strength at Break	236 MPa	34200 psi	ASTM D638
LNP Thermocomp® UF-1008 Polyphthalamide, Glass Fiber Reinforcement (discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..
Tensile Strength at Break	236 MPa	34200 psi	ASTM D638
SABIC Innovative Plastics LNP VERTON PX91060 PA 6 LNP* VERTON* PX91060 is a compound based on Nylon 6 resin containing Proprietary Fillers. Added feature of this grade is: Structural.
Tensile Strength at Break	236 MPa	34200 psi	ASTM D638
SABIC Innovative Plastics LNP VERTON PX91060 PA 6 (Asia Pacific) LNP* Verton* PX91060 is a compound based on Nylon 6 resin containing Long Glass Fiber.