LNP Thermocomp® UF-1008 Polyphthalamide, Glass Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Thermocomp® UF-1008 Polyphthalamide, Glass Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.55 g/cc
1.55 g/cc
Method A; ASTM D792
Water Absorption 0.20 %
0.20 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.012 cm/cm
0.012 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 236 MPa
34200 psi
ASTM D638
Tensile Strength, Yield 236 MPa
34200 psi
ASTM D638
Elongation at Break 2.1 %
2.1 %
ASTM D638
Elongation at Yield 2.1 %
2.1 %
ASTM D638
Tensile Modulus 16.1 GPa
2340 ksi
ASTM D638
Flexural Strength 310 MPa
45000 psi
ASTM D790
Flexural Modulus 13.4 GPa
1940 ksi
ASTM D790
Izod Impact, Notched 0.854 J/cm

@Thickness 3.18 mm
1.60 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 8.70 J/cm

@Thickness 3.18 mm
16.3 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 51.9 kJ/m²
24.7 ft-lb/in²
ISO 180
Falling Dart Impact 5.10 J
3.76 ft-lb
ASTM D3763
Processing Properties Metric English Comments
Melt Temperature 316 - 329 °C
601 - 624 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.15 %
0.15 %
Suggested
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi