- Polymer Property : Tensile Strength at Break = 5220 psi
Polymer Property : Tensile Strength at Break = 5220 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycolac® MG38U ABS High impact ABS. UL 746C f1 listed. Toughness/rigidity. Good fatigue resistance. |
|||
| Tensile Strength at Break | <= 36.0 MPa | <= 5220 psi | ISO/R527 |
| Polykemi AB POLYfill PP HIP15025 HC Polypropylene Information provided by Polykemi AB |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Geloy FXTW26SK ASA Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Geloy FXTW26SK ASA Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Geloy XTWM206 ASA (Asia Pacific) Next generation ASA optimized for outstanding weatherability, colorability and higher heat applications requiring UV exposure resistance.This data was supplied by SABIC-IP for the Asia Pacific regio.. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Geloy FXTW26SK ASA (Asia Pacific) Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Asia Pacific region... |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Geloy FXTW26SK ASA (Europe-Africa-Middle East) Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Europe-Africa-Middle.. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO R 527 |
| Fainplast Compounds RI 55 Rigid PVC, Injection Molding Fittings for building trade - high fluidity |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO 527 |
| GEHR Plastics PVC-ELS Polyvinylchloride, Electrically Conductive Grade Polyvinyl chloride is a flame retardant material with an exceptional chemical resistance and also with lower stress cracking. PVC-U shows high mechanical strength, tensile strength and the continuou.. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | Injection molded parts; DIN 53504 |
| Huntsman IROGRAN® A 92 E 4670 TPU-Polyester Introduction IROGRAN A 92 E 4670 is a thermoplastic polyester polyurethane for melt calendering. IROGRAN is part of the HUNTSMAN technical extrusion/injection molding product range and offers a spe.. |
|||
| Tensile Strength at Break | 36.0 MPa @Temperature 23.0 °C |
5220 psi @Temperature 73.4 °F |
50mm/min; ISO 527-2/1A/50 |
| SYNTHOS Forsan® 483 Acrylonitrile Butadiene Styrene (ABS) High heat resistant, high gloss.Applications: Electrotechnics, lighting equipment, automotiveHousehold appliances, electric switches, lamps, car interior parts, etc.Synthos was formerly known as Kau.. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp KZL34 POM LNP* Lubricomp* KZL34 is a compound based on Acetal resin containing Milled Glass and PTFE. Characteristic of this grade is Internally Lubricated.This data was supplied by SABIC-IP for the Americas.. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP MX06404 PP LNP LUBRICOMP* MX06404 is a compound based on Polypropylene resin containing 20% Glass Fiber and 15% PTFE. Added features of this material include: Heat Stabilized, Low Extractable, Wear Resistant... |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Xenoy® 364 PBT This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ASTM D638 |
| SABIC Innovative Plastics LNP STAT-LOY A3000 ABS LNP STAT-LOY* A3000 is a compound based on ABS resin. Added feature of this material is: Antistatic. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP 4X08423 FP-P (PFA) LNP* THERMOCOMP* 4X08423 is a compound based on PFA resin containing Glass Fiber. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO R 527 |
| Stir SpA HE 63/1 (PVC) Application: Economic profile for good fluidityInformation provided by STIR SpA |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | 0.2 in/min; ASTM Test |
| Styrolution Terblend® N NM-11 ABS/PA6 (Dry) Terblend N NM-11 is an ABS/PA6 blend combining very high impact strength, even at low temperatures, with an excellent processability and surface appearance.Information provided by STYROLUTION, which.. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | 0.2 in/min; ASTM Test |
| Styrolution Terblend® N NM-19 ABS/PA6 (Dry) Terblend N NM-19 is a UV stabilized ABS/PA6 blend combining very high impact strength, even at low temperatures with an excellent processability and surface appearance.Information provided by STYROL.. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP WX05505 PBT LNP* Thermocomp* WX05505 is a compound based on Thermoplastic Polyester (PBT) resin containing proprietary fillers. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP WBL36L PBT LNP* LUBRICOMP* WBL36L is a compound based on PBT resin containing 30% Glass Bead, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO 527 |
| SABIC Innovative Plastics LNP STAT-LOY K3000Z Acetal LNP* STAT-LOY* K3000Z is a compound based on unfilled Acetal resin. Added feature of this material is: Antistat. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO 527-3/5/500 |
| Lubrizol Estane® 54611 Polyester-Based Thermoplastic Polyurethane Feature: Facilitates to produce high coating weight in one pass high production speed. Broad process window and transparent spherical pellets.Uses: Melt roll coated fabrics and unsupported foils.Av.. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | 50mm/min; ISO 527-2 |
| Denka TH-11 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | 50mm/min; ISO 527-2 |
| Denka TH-21 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ISO R 527 |
| Fainplast Compounds R 316/AS Rigid PVC, Extrusion Antistatic profiles |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ASTM D638 |
| Arkema Group Pebax® 4033 Polyether Block Amide (PEBA) Typical application: Mechanical partsInformation provided by Arkema Group |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ASTM-D638 |
| Braskem GD5160 HDPE Blow Molding Polyethylene Homopolymer GD5160 is a high-density polyethylene homopolymer with high density and stiffness combined with high impact resistance and productivity. It was developed for the blow-molding segment. It is used in .. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ASTM D638 |
| Asahi Glass Fluon® P-65P PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
| Tensile Strength at Break | 36.0 MPa | 5220 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Cycolac® DL100LG ABS (Europe-Africa-Middle East) Cycolac DL100LG is a low gloss, high heat, high impact ABS/PC blend with low emission |
|||