Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Cycoloy® CE8510 PC+ABS (Europe-Africa-Middle East) Extrusion grade PC/ABS. Low viscosity, high impact and ductility.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycoloy® XCY620S PC+ABS (Europe-Africa-Middle East) PC+ ABS automotive applications, excellent flow/impact balance, high heat resistance temperature and excellent properties retention after hydrolytic and heat aging. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics GELOY HRA222 ASA+PC (Europe-Africa-Middle East) GELOY HRA222 is a multi-purpose, chlorine and bromine free flame retardant ASA+PC alloy for injection moulding processes. Typical properties as measured on natural material. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® CFR9712 PC COPOLYMER (Europe-Africa-Middle East) Lexan* CFR9712 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 2.0 mm and high flow capability. .. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® EXL1112T PC Copolymer (Asia Pacific) Lexan* EXL1112T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade. This resin offers good low temperature (-20 C) ductility in combination with high flow char.. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® EXL1162T PC Copolymer Lexan* EXL1162T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade with extra release properties. This resin offers good low temperature (-20 C) ductility in c.. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® EXL1192T PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1192T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade with extra release properties for food contact applications. This resin offers good low temp.. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FXE1112T PC Copolymer (Asia Pacific) Lexan* FXE1112T Lexan* polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers good low temperature (-20 C) ductility in combination with high flow ch.. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD1830 PC Copolymer 40 MFR LEXAN High Flow Ductile Copolymer UV Stabilized |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HPF0 PC Copolymer 40 MFR LEXAN High Flow Ductile Copolymer Healthcare Grade |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HPX8R PC Copolymer Very high flow specialty polycarbonate with outstanding processability and ductility. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 o.. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP FARADEX KX88084 POM (Europe-Africa-Middle East) LNP* Faradex* KX88084 is a compound based on POM resin containing Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® CFR9712 PC COPOLYMER (Asia Pacific) Lexan* CFR9712 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 2.0 mm and high flow capability. .. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD1810 PC Copolymer (Europe-Africa-Middle East) 40 MFR LEXAN High Flow Ductile Copolymer |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HFD4472 PC Lexan* HFD4472 is a 20% glass filled, medium flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4472 has enhanced mold release, impact ductili.. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRILOY RA2 PA 66 (Asia Pacific) LNP* Lubriloy* RA2 is a compound based on Nylon 66 resin containing Aramid Fiber. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Xenoy® 1731 PBT+PC Impact/chemical resistant. UV-Stabilized. Excellent physical property retention in automotive exteriors and OVAD. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® CL100 PBT+PC Xenoy CL100 is an unfilled, impact modified, UV-stabilized PC/PBT blend with excellent solvent resistance and good low-temperature ductility. It has a proven track record in unpainted exterior autom.. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Noryl NH3060 PPE+HIPS NH3060 resin is a modified PPE + PS blend with an excellent balance of non-chlorinated non-brominated flame retardance, hydrolytic stability, impact and heat resistance, good flow, and low specific .. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL NH6020 PPE+HIPS Noryl NH6020 resin is an unfilled, injection moldable modified polyphenylene ether resin. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 0.8 .. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL EXNL0353 PPE+HIPS EXNL0353 resin is a modified PPE + PS blend with an excellent balance of non-halogenated flame retardance, hydrolytic stability, impact and heat resistance, good flow, and low specific gravity for l.. |
|||
Tensile Strength at Break | >= 56.0 MPa | >= 8120 psi | ASTM D638 |
UBE UBESTA® 3020LU1X3 Rigid Black Electronic Grade Nylon 12 Description: UBESTA Nylon 12 has an excellent termite resistance than other plastics. UBESTA contributes as a material for jacket and sheath which lay for telephone and telegram Communication System.. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | ISO 527-1 |
Vyncolit TX10916/15 Graphite Filled Novolac Phenolic Novolac resin based, graphite filled compound used for low friction applications where dimensional stability is requiredInformation provided by Sumitomo Bak North America, Inc. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | ASTM D638 |
Toyobo VYLOPET® EMC307 Injection Molding Polyester Resin, High Cycles Applications: Coiled bobbinsMouthpiecesFeatures: High cyclesInformation provided by Toyobo. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 5 mm/min; ISO 527-2 |
BASF Ultradur® B 6550 LN PBT Description: High-viscosity grades for the extrusion of loose buffer tubes for optical fibers, semi-finished products for machining, profiles and pipes.Information provided by BASF |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® EXRL0672 PC Copolymer 40 MFR LEXAN High Flow Ductile CopolymerThis data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 5mm/min; ISO 527-2/1A/5 |
SYNTHOS Krasten® 171 General Purpose Polystyrene Very good heat resistance and mechanical strength. Examples of Application:Extrusion – biaxial-oriented sheets BOPS, XPS – lightweight insulating boards, shower enclosure panels, blends with high .. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 5mm/min; ISO 527-2/1A/5 |
SYNTHOS Krasten® 172 General Purpose Polystyrene Very good heat resistance and mechanical strength. Examples of Application:Extrusion – cups for hot drinks, shower enclosure panels, lightweight XPS sheets. Blends with high impact polystyrene, SBS.. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50mm/min; ASTM D638 |
3M Dyneon™ PVDF 31008/0003 Polyvinylidene Fluoride
(discontinued **) 3M™ Dyneon™ PVDF 31008/0003 is a flexible copolymer of VF2 and CTFE, exhibiting very low shrinkage and excellent impact resistance. Dyneon PVDF 31008/0003 also has a very low brittleness temperatu.. |
|||
Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL FE8000S PPE+PS Noryl* FE8000S resin is an unfilled modified polyphenylene ether resin designed for fluid handling applications. This resin is suitable for multiple conversion routes and will be available in custom.. |