Polymer Property : Tensile Strength at Break = 7100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	49.0 MPa	7100 psi	2 in/min; ASTM D638
RheTech Products G10P100-00 10% Glass Fiber Reinforced Polypropylene, Natural Applications: BracketsIP structural componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	49.0 MPa	7100 psi	2 in/min; ASTM D638
RheTech Products G10P100-01 10% Glass Fiber Reinforced Polypropylene, Black Applications: BracketsIP structural componentsDome light housingInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	49.0 MPa	7100 psi	2 in/min; ASTM D638
RheTech Products G10P100-01UV 10% Glass Fiber Reinforced Polypropylene, UV Stabilized, Black Applications: BracketsIP structural componentsDome light housingInjection molding conditions reported in table.Information provided by RheTech Products.
Tensile Strength at Break	49.0 MPa	7100 psi	ASTM D638
Polymer Resources PC/TP-FR3 Flame Retardant PC/Polyester Alloy Flame Retardant, High Impact, Excellent Chemical ResistanceFeatures: • Flame Retardant • Impact Modified • Self Extinguishing • Good Chemical ResistanceProcess: Injection MoldingNotes: All p..
Tensile Strength at Break	49.0 MPa	7100 psi	ASTM D638
Polymer Resources PPX-FR2 Modified-PPO, V-1 Flame Retardant Modified-Polyphenylene Oxide, V-1 Flame Retardant, 210F HDTFeatures: • Bromine Free • Chlorine FreeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-..
Tensile Strength at Break	49.0 MPa	7100 psi	ASTM D638
Polymer Resources PPX-FR2-[color]-EN Modified-PPO, V-1 Flame Retardant, Extrusion Grade Modified-Polyphenylene Oxide, V-1 Flame Retardant, 210F HDT, Extrusion GradeFeatures: • Bromine Free • Chlorine FreeProcess: ExtrusionNotes: All physical, mechanical and thermal testing conducte..
Tensile Strength at Break	49.0 MPa	7100 psi	ASTM D638
Polymer Resources TP-FV699 PBT, 10% Glass Reinforced Structural Foam Grade, Low Shrinkage Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel..
Tensile Strength at Break	49.0 MPa	7100 psi	ASTM D638
Chase Plastics CP Pryme® A100 ABS Molding Resin Information provided by Chase Plastics.
Tensile Strength at Break	49.0 MPa	7100 psi	ASTM D638
Chase Plastics CP Pryme® A100HF ABS Molding Resin, High Flow Information provided by Chase Plastics.
Tensile Strength at Break	49.0 MPa	7100 psi	ASTM D638
Plastics Group Polifil® GFPP-30 30% Glass-Reinforced Polypropylene Polifil® GFPP series compounds are homopolymer polypropylene resins reinforced with glass fibers. They provide high impact with increased strength, stiffness, surface hardness, and higher continuou..
Tensile Strength at Break	49.0 MPa	7100 psi	Lower curing cycle, lower heat resistance
Abatron AboCast/AboCure 50-7/8501-4 High Temperature Resistant Epoxy Clear amber, high viscosity, structural/dielectric epoxy with high temperature resistance.Suggested Uses: Casting, bonding, potting, encapsulation of electric, structural and industrial components t..