Polymer Property : Tensile Stress = 34.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Stress	34.0 MPa	4930 psi	at Break; ISO 527
Iran Petrochemical (PCC) BL 4M HM 8355 High Density Polyethylene BL4M is a high density polyethylene with 1-Butene as co monomer. It is high molar mass, easily processable, high stiffness and strength, good SCR, very good molding surface finish.Applications: jer..
Tensile Stress	34.0 MPa	4930 psi	ISO R527
Iran Petrochemical (PCC) C 30 S Polypropylene Polypropylene homopolymer with a good flow properties.Applications: film, yarn, monofilament, cast film and sheetsInformation provided by Iran Petrochemical Commercial Co.
Tensile Stress	34.0 MPa	4930 psi	ISO R527
Iran Petrochemical (PCC) Moplen EP-S31HP Polypropylene Moplen EP-S31HP is a heterophasic polypropylene copolymer with an exceptional mechanical properties balance. In comparison with standard polypropylene copolymers with the same fluidity, Moplen EP-..
Tensile Stress	34.0 MPa	4930 psi	ISO R527
Iran Petrochemical (PCC) T 30 S Polypropylene T30S is a polypropylene homopolymer particularly suitable for the extrusion of sheet for thermoforming, film yarn and mono filament.Applications: T30S is designed for bags industrial fabrics and mat..
Tensile Stress	34.0 MPa	4930 psi	ISO R527
Iran Petrochemical (PCC) X 30 G Polypropylene X30G is for injection molding because of its good flow properties this grade offers easy processing and extruded items exhibit high stiffness.Applications: The grade is widely used for injection mol..
Tensile Stress	34.0 MPa	4930 psi	ISO R527
Iran Petrochemical (PCC) X 30 S Polypropylene Film Polypropylene film with good optical propertiesApplications: film, packing food stuffs, stationary and textiles.Information provided by Iran Petrochemical Commercial Co.
Tensile Stress	34.0 MPa	4930 psi	50 mm/min; ISO 527-1,-2
Inno-Comp INNOPOLÂ® CS 1-2120 AP 20% Talc Filled Polypropylene Homopolymer INNOPOL CS 1-2120 AP is a 20 % talc filled compound based on polypropylene homopolymer. This grade is available in natural and custom colored form.INNOPOLÂ® CS 1-2120 AP is recommended especially..