Polymer Property : Izod Impact, Notched (ISO) = 0.809 ft-lb/in² Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Izod Impact, Notched (ISO)	1.70 kJ/m² @Thickness 4.00 mm, Temperature 23.0 °C	0.809 ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F	ISO 180/1A
Polimeri Europa Edistir N 1782 Polystyrene General purpose polystyrene with good flow and high heat resistance. Suggested for direct gassing extrusion of heavy gage insulating boards (XPS) and in blend with high concentration of clear SBS f..
Izod Impact, Notched (ISO)	1.70 kJ/m² @Thickness 4.00 mm, Temperature 23.0 °C	0.809 ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F	ISO 180/1A
Polimeri Europa Edistir N 1840 Polystyrene General purpose polystyrene combining easy flow and medium heat. Edistir N 1840 is suggested in extrusion for glossy capping of HIPS sheets and for blending with HIPS or clear SBS for stiffer therm..
Izod Impact, Notched (ISO)	1.70 kJ/m² @Thickness 4.00 mm, Temperature -30.0 °C	0.809 ft-lb/in² @Thickness 0.157 in, Temperature -22.0 °F	ISO 180/1A
Polimeri Europa Edistir N 2380 Polystyrene High molecular weight general purpose polystyrene combining high heat resistance and good mechanical strength. Suitable for direct gassing extrusion, for biaxially oriented films and sheets, for gla..
Izod Impact, Notched (ISO)	1.70 kJ/mÂ² @Temperature -40.0 Â°C	0.809 ft-lb/inÂ² @Temperature -40.0 Â°F	ISO 180
LyondellBasell Hostacomâ„¢ BC142/1AC Polypropylene Copolymer Description: Hostacomâ„¢ BC142/1AC conventional melt flow, 3,600 MPa flexural modulus, precolored, mineral-filled polypropylene copolymer has a good balance of stiffness and impact resistance. It..
Izod Impact, Notched (ISO)	1.70 kJ/m² @Thickness 4.00 mm, Temperature 23.0 °C	0.809 ft-lb/in² @Thickness 0.157 in, Temperature 73.4 °F	ISO 180/1A
Polimeri Europa Edistir N 1910 Polystyrene Very easy flow general purpose polystyrene. Used for injection of thin-wall, multi-cavity, very fast-cycle mouldings and for sheet extrusion in glossy capping of HIPS and in blend with HIPS or clear..