Polymer Property : Tensile Strength at Break = 2570 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	17.7 MPa @Thickness 2.00 mm, Temperature 23.0 °C	2570 psi @Thickness 0.0787 in, Temperature 73.4 °F	Type 2, 200 mm/min Across Flow; ISO 37
PolyOne OnFlex™ U 5370A-E0077 Thermoplastic Elastomer (TPE) OnFlex™ U thermoplastic elastomer compounds are based on thermoplastic polyurethane elastomers (TPE-U). The OnFlex™ U 5300 series are based upon alloys of SEBS and TPU, combining the advantages of..
Tensile Strength at Break	17.7 MPa @Thickness 2.00 mm, Temperature 23.0 °C	2570 psi @Thickness 0.0787 in, Temperature 73.4 °F	Type 2, 200 mm/min; Flow; ISO 37
PolyOne OnFlex™ U 5370A-E0077 Thermoplastic Elastomer (TPE) OnFlex™ U thermoplastic elastomer compounds are based on thermoplastic polyurethane elastomers (TPE-U). The OnFlex™ U 5300 series are based upon alloys of SEBS and TPU, combining the advantages of..
Tensile Strength at Break	17.7 MPa @Temperature 150 Â°C, Time 1190 sec	2570 psi @Temperature 302 Â°F, Time 0.330 hour	Cured
LG Chemical NBR 3250 High Acrylonitrile Polymer Description: NBR 3250 is a copolymer of butadiene and acrylonitrile manufactured by cold emulsion polymerization technology of Goodyear Tire and Rubber Company, USA. NBR 3250 is a non staining, medi..