Polymer Property : Tensile Strength at Break = 2650 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	18.3 MPa @Treatment Temp. 100 Â°C, Time 252000 sec	2650 psi @Treatment Temp. 212 Â°F, Time 70.0 hour	Aged ASTM D #1 Oil
LG Chemical NBR 3250 High Acrylonitrile Polymer Description: NBR 3250 is a copolymer of butadiene and acrylonitrile manufactured by cold emulsion polymerization technology of Goodyear Tire and Rubber Company, USA. NBR 3250 is a non staining, medi..
Tensile Strength at Break	18.3 MPa @Temperature 100 Â°C, Time 259000 sec	2650 psi @Temperature 212 Â°F, Time 72.0 hour	Circulating Oven Aging
LG Chemical NBR 6230 High Acrylonitrile Polymer Description: NBR 6230 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6230 is a non staining, low mooney, and m..
Tensile Strength at Break	18.3 MPa @Temperature 145 Â°C, Time 1190 sec	2650 psi @Temperature 293 Â°F, Time 0.330 hour	Cured
LG Chemical NBR 6240 High Acrylonitrile Polymer Description: NBR 6240 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6240 is a non staining, medium low mooney..