LG Chemical NBR 6240 High Acrylonitrile Polymer
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical NBR 6240 High Acrylonitrile Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: NBR 6240 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6240 is a non staining, medium low mooney, and medium high acrylonitrile polymer designed to aid in processing operations such as extruding and calendaring. NBR 6240 is a low temperature polymerized polymer, and such as, retains the excellent physical and processing properties of a cold nitrile rubber. Applications: NBR 6240 is recommended to use in packings, shoe products, chemically blown sponge, oil field products, industrial and automotive molded parts.CAS No: 9003-18-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.990 g/cc | 0.990 g/cc | |
| Volatiles | 0.30 % | 0.30 % | |
| Mooney Viscosity | 41 @Temperature 100 °C |
41 @Temperature 212 °F |
ML 1+4 |
| Ash | <= 0.50 % | <= 0.50 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 69 @Temperature 145 °C, Time 1190 sec |
69 @Temperature 293 °F, Time 0.330 hour |
Cured |
| 73 @Temperature 100 °C, Time 259000 sec |
73 @Temperature 212 °F, Time 72.0 hour |
Circulating Oven Aging | |
| 45 @Treatment Temp. 25.0 °C, Time 259000 sec |
45 @Treatment Temp. 77.0 °F, Time 72.0 hour |
Aged fuel C | |
| 69 @Treatment Temp. 100 °C, Time 259000 sec |
69 @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #3 Oil | |
| 73 @Treatment Temp. 100 °C, Time 259000 sec |
73 @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #1 Oil | |
| Tensile Strength at Break | 18.3 MPa @Temperature 145 °C, Time 1190 sec |
2650 psi @Temperature 293 °F, Time 0.330 hour |
Cured |
| 18.9 MPa @Temperature 100 °C, Time 259000 sec |
2740 psi @Temperature 212 °F, Time 72.0 hour |
Circulating Oven Aging | |
| 28.3 MPa @Temperature 145 °C, Time 2990 sec |
4100 psi @Temperature 293 °F, Time 0.830 hour |
cured; ASTM D412 | |
| 13.4 MPa @Treatment Temp. 25.0 °C, Time 259000 sec |
1940 psi @Treatment Temp. 77.0 °F, Time 72.0 hour |
Aged fuel C | |
| 18.8 MPa @Treatment Temp. 100 °C, Time 259000 sec |
2730 psi @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #1 Oil | |
| 18.8 MPa @Treatment Temp. 100 °C, Time 259000 sec |
2730 psi @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #3 Oil | |
| Elongation at Break | 373.2 % @Temperature 100 °C, Time 259000 sec |
373.2 % @Temperature 212 °F, Time 72.0 hour |
Circulating Oven Aging |
| 400 % @Temperature 145 °C, Time 1190 sec |
400 % @Temperature 293 °F, Time 0.330 hour |
Cured | |
| 575 % @Temperature 145 °C, Time 2990 sec |
575 % @Temperature 293 °F, Time 0.830 hour |
cured; ASTM D412 | |
| 353.1 % @Treatment Temp. 25.0 °C, Time 259000 sec |
353.1 % @Treatment Temp. 77.0 °F, Time 72.0 hour |
Aged fuel C | |
| 372.3 % @Treatment Temp. 100 °C, Time 259000 sec |
372.3 % @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #1 Oil | |
| 377 % @Treatment Temp. 100 °C, Time 259000 sec |
377 % @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #3 Oil | |
| 300% Modulus | 0.0121 GPa @Temperature 145 °C, Time 2990 sec |
1.75 ksi @Temperature 293 °F, Time 0.830 hour |
cured; ASTM D412 |
| Rebound | 43.1 % @Temperature 30.0 °C |
43.1 % @Temperature 86.0 °F |
|
| Abrasion | 0.2895 | 0.2895 | AKRON |
| Compression Set | 21.1 % @Temperature 100 °C, Time 259000 sec |
21.1 % @Temperature 212 °F, Time 72.0 hour |
160°C x 30 min. Cured) |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Bound AN Content | 0.34 | |
| Color | Tan | |
| Components | HAF (IRB#7) | 40 phr, ASTM D3187 |
| NBR 6240 | 100 phr, ASTM D3187 | |
| Stearic Acid | 1 phr, ASTM D3187 | |
| Sulfur | 1.5 phr, ASTM D3187 | |
| TBBS | 0.7 phr, ASTM D3187 | |
| ZnO | 3 phr, ASTM D3187 | |
| Compound Recipe | Antioxidant(3-C) | 1 phr |
| Antioxidant(RD) | 2 phr | |
| Carbon Black(SRF) | 80 phr | |
| CZ | 2 phr | |
| NBR 6240 | 100 phr | |
| Plasticizer(DOP) | 10 phr | |
| Stearic Acid | 1 phr | |
| Sulfur | 0.5 phr | |
| TT | 1 phr | |
| Zinc Oxide | 5 phr | |
| Rheometer | 1.1 min | ts1, 160°C x 12 min, 1° Arc, MDR |
| 1.2 min | t'50, 160°C x 12 min, 1° Arc, MDR | |
| 1.4 lb-in | ML, 160°C x 12 min, 1° Arc, MDR | |
| 2.8 min | t'90, 160°C x 12 min, 1° Arc, MDR | |
| 23.6 lb-in | MH, 160°C x 12 min, 1° Arc, MDR | |
| Volume Swell | -0.028 | Aged ASTM D #3 Oil (100°C x 72hrs) |
| -0.068 | Aged ASTM D #1 Oil (100°C x 72hrs) | |
| 0.408 | Aged fuel C (RT°C x 72hrs) |