Polymer Property : Tensile Strength at Break = 2730 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	18.8 MPa @Treatment Temp. 100 Â°C, Time 259000 sec	2730 psi @Treatment Temp. 212 Â°F, Time 72.0 hour	Aged ASTM D #3 Oil
LG Chemical NBR 7150 High Acrylonitrile Polymer Description: NBR 7150 is a copolymer of butadiene and acrylonitrile manufactured by cold emulsion polymerization technology of Goodyear Tire and Rubber Company, USA. NBR 7150 is a non staining, medi..
Tensile Strength at Break	18.8 MPa @Treatment Temp. 100 Â°C, Time 259000 sec	2730 psi @Treatment Temp. 212 Â°F, Time 72.0 hour	Aged ASTM D #1 Oil
LG Chemical NBR 6240 High Acrylonitrile Polymer Description: NBR 6240 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6240 is a non staining, medium low mooney..
Tensile Strength at Break	18.8 MPa @Treatment Temp. 100 Â°C, Time 259000 sec	2730 psi @Treatment Temp. 212 Â°F, Time 72.0 hour	Aged ASTM D #3 Oil
LG Chemical NBR 6240 High Acrylonitrile Polymer Description: NBR 6240 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6240 is a non staining, medium low mooney..