- Polymer Property : K (wear) Factor = 28.2 x 10-8 mm³/N-M
Polymer Property : K (wear) Factor = 28.2 x 10-8 mm³/N-M Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| SABIC Innovative Plastics LNP LUBRICOMP DFL36P PC LNP* Lubricomp* DFL36P is a compound based on Polycarbonate containing 30% Glass Fiber 15% PTFE. Added features include: Exceptional Processing. Internally Lubricated. |
|||
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Dry: 0.25 m/s, 3.4 MPa (50 fpm, 500 psi); ASTM D3702 |
| Solvay Specialty Polymers Torlon® 4301 Polyamide-imide (PAI)
(Unverified Data**) Torlon 4301 is a wear-resistant grade of polyamide-imide (PAI) resin. It has a good balance of mechanical properties and wear resistance. It offers high flexural and compressive strength with a low .. |
|||
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| SABIC Innovative Plastics LNP LUBRICOMP ICL34 PA6.12 LNP* LUBRICOMP* ICL34 is a compound based on Nylon 6/12 containing 20% Carbon Fiber, 15% PTFE. Added features include: Wear Resistant. |
|||
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| SABIC Innovative Plastics LNP LUBRICOMP KL003LH Acetal LNP* LUBRICOMP* KL003LH is an Acetal based compound containing 15% PTFE. Added features of this grade include: Low Extractable, Healthcare, Wear Resistant. |
|||
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| SABIC Innovative Plastics LNP LUBRICOMP LCL33EXQ PEEK LNP* LUBRICOMP* LCL33EXQ is a compound based on Polyetheretherketone containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Easy Molding. |
|||
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| SABIC Innovative Plastics LNP LUBRICOMP RFP38 PA6.6 LNP* LUBRICOMP* RFP38 is a compound based on Nylon 66 containing 40% Glass Fiber, 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant. |
|||
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| SABIC Innovative Plastics LNP LUBRICOMP SCP36 PA12 LNP* LUBRICOMP* SCP36 is a compound based on Nylon 12 containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Wear Resistant, Electrically Conductive. |
|||
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| SABIC Innovative Plastics LNP LUBRICOMP SFP36 PA12 LNP* LUBRICOMP* SFP36 is a compound based on Nylon 12 resin containing 30% Glass Fiber 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant. |
|||
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| SABIC Innovative Plastics LNP THERMOCOMP RC008 PA 66 LNP THERMOCOMP* RC008 is a compound based on Nylon 66 resin containing 40% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| SABIC Innovative Plastics LNP STAT-LOY K3000SZ Acetal Copoly LNP* STAT-LOY* K3000SZ is a compound based on Acetal Copolymer resin. Added feature of this material is: AntiSstatic. |
|||
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| SABIC Innovative Plastics LNP STAT-LOY K3000SZ Acetal Copoly (Asia Pacific) LNP* Stat-loy* K3000SZ is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat. |
|||
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| SABIC Innovative Plastics LNP STAT-LOY K3000Z Acetal LNP* STAT-LOY* K3000Z is a compound based on unfilled Acetal resin. Added feature of this material is: Antistat. |
|||
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | K=W/PVT where W=wear (inches^3); P=applied pressure (psi); V=velocity (fpm); T=time (hours). |
| A. Schulman ComAlloy E-13370B Internally Lubricated, Glass Fiber Reinforced Polyester Alloy Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||
| K (wear) Factor | 28.2 x 10-8 mm³/N-M | 14.0 x 10-10 in³-min/ft-lb-hr | K=W/PVT where W=wear (inches^3); P=applied pressure (psi); V=velocity (fpm); T=time (hours). |
| A. Schulman ComAlloy Lubrilon® 629 Nylon 6/6, Glass Fiber/PTFE Filled, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||