Polymer Property : Tensile Strength, Yield = 724 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	>= 724 MPa @Strain 0.200 %	>= 105000 psi @Strain 0.200 %	H1150 Condition - 620Â°C at 4 hr
Latrobe LescalloyÂ® 17-4 VAC-ARC Precipitation Hardening Stainless Steel LESCALLOY 17-4 VAC-ARC steel is a precipitation hardening martensitic stainless steel. A wide range of mechanical properties is available via simple aging within a 900-1150Â°F (482-621Â°C) tempe..
Tensile Strength, Yield	724 MPa @Strain 0.200 %	105000 psi @Strain 0.200 %	5.25 in. Test Specimen
Latrobe LescalloyÂ® 410Cb High Strength Stainless Steel LESCALLOY 17-4 VAC-ARC steel is a precipitation hardening martensitic stainless steel. A wide range of mechanical properties is available via simple aging within a 900-1150Â°F (482-621Â°C) tempe..
Tensile Strength, Yield	724 MPa @Strain 0.200 %, Thickness <=38.1 mm	105000 psi @Strain 0.200 %, Thickness <=1.50 in	Tension
Crucible Steel Aquamet® 19 Stainless Steel AQUAMET 19 is a modified Type 304 stainless steel that is fully austenitic and non-magnetic. Strengthened by adding nitrogen to the melt, it has better corrosion resistance than Type 304 stainless. ..
Tensile Strength, Yield	>= 724 MPa @Strain 0.200 %	>= 105000 psi @Strain 0.200 %	AMS 5542 aged, sheet
ATI Allegheny Ludlum Altemp® X-750 Nickel-Based superalloy Characteristics: precipitation hardenable, high strength up to 1300°F, oxidation resistant up to 1800°F. Applications: aerospace, heat treatment fixtures, forming tools, extrusion dies.Information..
Tensile Strength, Yield	>= 724 MPa @Strain 0.200 %	>= 105000 psi @Strain 0.200 %	AMS 5598 aged, plate
ATI Allegheny Ludlum Altemp® X-750 Nickel-Based superalloy Characteristics: precipitation hardenable, high strength up to 1300°F, oxidation resistant up to 1800°F. Applications: aerospace, heat treatment fixtures, forming tools, extrusion dies.Information..