Polymer Property : Film Tensile Strength at Break, MD = 8700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	Orientation not specified; ASTM D882
Nylene® 615 Nylon 6, Film Grade Film Grade. Nylene 615 is an extrusion grade nylon 6 resin suitable for coating and film co-extrusion applications. It has excellent melt stability and good melt strength. Nylene 615 has superior ..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	Orientation not specified; ASTM D882
Nylene® 615I Nylon 6, Film Grade Film Grade. Nylene 615I is an extrusion grade nylon 6 resin suitable for film co- extrusion applications and blown film. It has excellent melt stability and good melt strength. Nylene 615I has supe..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	Orientation not specified; ASTM D882
Nylene® 615SA Nylon 6, Film Grade Film Grade. Nylene 615SA is a Kosher, extrusion grade nylon 6 resin suitable for film co-extrusion applications and blown film. It has excellent melt stability and good melt strength. Nylene 615SA..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	Orientation not specified; ASTM D882
Nylene® NX3055I Nylon 6 Dry as molded. Film Grade. Nylene NX3055I is an extrusion grade nylon 6 suitable for cast film, blown film, and co-extrusion applications. NX3055I is highly crystalline which yields excellent roll..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	Orientation not specified; ASTM D882
Nylene® NX3411 Nylon 6 Film Grade. Nylene NX3411 is an extrusion grade nylon 6 resin suitable for film co-extrusion applications and blown film. It has excellent melt stability and good melt strength. Nylene NX3411 has ..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
SABIC F00952 High Density Polyethylene for Blown Film Product Description: F00952 is a high molecular weight high density polyethylene copolymer grade specifically designed for blown film applications. Its high molecular weight, broad molecular weigh..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
SABIC FJ00952 High Density Polyethylene for Blown Film Product Description: FJ00952 is a TNPP additive free, high molecular weight high density polyethylene copolymer grade specifically designed for blown film applications. Its high molecular weight, ..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
Eastman 9921P PET Film (discontinued **) Voridian PET 9921P is produced at Voridian’s manufacturing sites in Rotterdam and Zarate, it is PTA/CHDM based, and it is sold to customers in the Europe, Middle East and Africa, Argentina, Bolivia..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
ExxonMobil Exceed™ 377D60 LDPE/Hexene Tough Premium Film Resin, 0.8 mil Film (discontinued **) Data provided by the manufacturer, Exxon Chemical.A hexene copolymer produced using Exxon Chemical's EXXPOL® technology. Films made from EXCEED 377D60 resin exhibit excellent impact strength and b..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ISO 527-3
Total PPH 6088 Polypropylene Homopolymer, Cast Film Polypropylene PPH 6088 is a homopolymer polypropylene with a Melt Flow index of 9 g/10 min for the cast extrusion of film with excellent optical properties and good sterilizability.Polypropylene PPH..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
Formosa Plastics Formolene® E924ND Film HDPE High Molecular Weight High Density Polyethylene (HMW-HDPE) for Film Extrusion Formolene® E924ND is a bi-modal HMW-HDPE resin designed for high dart impact strength and good processing characteristi..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
ExxonMobil Enable™ 20-05HE Metallocene Polyethylene Resin Product Description: Enable 20-05 resins are metallocene ethylene-hexane copolymers. Enable mPE resins offer an outstanding balance between processing and film properties, including tensile, impact ..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
ExxonMobil Enable™ 20-05HH Metallocene Polyethylene Resin (Asia Pacific Grade) Product Description: Enable 20-05 resins are metallocene ethylene-hexene copolymers. Enable mPE resins offer an outstanding balance between processing and film properties, including tensile, impact ..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
ExxonMobil Enable™ 20-05HH Metallocene Polyethylene Resin (European Grade) Product Description: Enable 20-05HH is a metallocene ethylene-hexene copolymer. Enable mPE resins offer an outstanding balance between processing and film properties, including tensile, impact and p..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
ExxonMobil Exceed™ 2018HA Metallocene Polyethylene Resin (European Grade) Product Description: Exceed 2018HA is a metallocene Catalyzed ethylene-hexene copolymer. Films made from Exceed 2018HA have outstanding tensile, impact strength, and puncture. These superior strengt..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
ExxonMobil LLDPE LL 1201KG Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 1201 series are LLDPE grades, offering excellent combination of stiffness and optical properties (when blended with 10-20% LDPE) Availability: Africa & Middle East, Asia Paci..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
ExxonMobil LLDPE LL 1201XV Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 1201 series are LLDPE grades, offering excellent combination of stiffness and optical properties (when blended with 10-20% LDPE) Availability: Africa & Middle East, Asia Paci..
Film Tensile Strength at Break, MD	60.0 MPa @Thickness 0.0150 mm	8700 psi @Thickness 0.000591 in	ASTM D882
Equate EGDA-6888 HDPE Film Extrusion Resin EGDA-6888 is a high molecular weight, high density polyethylene copolymer that has been designed specifically for tubular film extrusion. Its broad molecular weight distribution and density have bee..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi
Dow DOWLEX™ NG 3347A Linear Low Density Polyethylene, Ethylene-Octene Copolymer Next Generation DOWLEX® NG 3347A resin with extra stretch performance (ESP)is an ethylene-octene-1 copolymer designed for cast stretch film applications such as industrial pallet wrap. DOWLEX NG 33..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
ExxonMobil Enable™ 20-05HE Metallocene Polyethylene Resin (Asia Pacific Grade) Product Description: Enable 20-05 resins are metallocene ethylene-hexene copolymers. Enable mPE resins offer an outstanding balance between processing and film properties, including tensile, impact ..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
ExxonMobil Enable™ 20-05HH Metallocene Polyethylene Resin Product Description: Enable 20-05 resins are metallocene ethylene-hexane copolymers. Enable mPE resins offer an outstanding balance between processing and film properties, including tensile, impact ..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
ExxonMobil Enable™ 20-05CB Metallocene Polyethylene Resin Product Description: Enable 20-05 resins are metallocene ethylene-hexane copolymers. Enable mPE resins offer an outstanding balance between processing and film properties, including tensile, impact ..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
ExxonMobil Enable™ 35-05CH Metallocene Polyethylene Resin (European Grade) Product Description: Enable 35-05CH is a metallocene ethylene-hexene copolymers. Enable mPE resins offer an outstanding balance between processing and film properties, including tensile, impact and ..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	ASTM D882
Braskem HF 0144 HDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Grocery and T-shirt bags; merchandise bags; frozen-food bags. Information provided by Bras..
Film Tensile Strength at Break, MD	60.0 MPa	8700 psi	cast films; ISO 527-3
Borealis Bormod™ HC904CF Polypropylene Bormod™ BJ368MO is a polypropylene copolymer characterized by good flow, and optimum combination of high stiffness and high impact strength. The material is nucleated with Borstar® Nucleation Tech..