Polymer Property : Tensile Strength, Yield = 120 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	0.827 - 23.4 MPa	120 - 3400 psi	Average value: 11.1 MPa Grade Count:379
Overview of materials for PVC, Flexible Grade This property data is a summary of similar materials in the MatWeb database for the category "PVC, Flexible Grade". Each property range of values reported is minimum and maximum values of appropriat..
Tensile Strength, Yield	0.827 MPa @Strain 100 %	120 psi @Strain 100 %	ASTM D412
Multibase Multi-FlexÂ® A 4001 LC Black TPE Thermoplastic Elastomer Features: Heat Resistance, HighOzone ResistantCompression Set, Low Forms: PelletsProcessing Method:Injection Molding Information provided by Multibase
Tensile Strength, Yield	0.827 MPa	120 psi	at 100% secant; ASTM D412
Multibase Multi-FlexÂ® A 4001 LC TPE Thermoplastic Elastomer Features: Chemical Resistance, GoodCompressive Strength, GoodHeat Resistance, MediumOzone ResistantThermal Stability, GoodForms:PelletsProcessing Methods:Injection MoldingExtrusion Information pro..
Tensile Strength, Yield	0.827 MPa @Strain 100 %	120 psi @Strain 100 %	ASTM D412
Multibase Multi-FlexÂ® A 4001 LCS Black TPE Thermoplastic Elastomer Forms: PelletsProcessing Method:Injection Molding Information provided by Multibase
Tensile Strength, Yield	0.827 MPa	120 psi	ASTM D-412 (Die C)
Saint-Gobain Norcrylâ„¢ A1000 Solid Acrylic Bonding Tape Description: The Norcrylâ„¢ solid acrylic core has outstanding internal strength. Norcrylâ„¢ structural grade bonding power can reduce or replace conventional fasteners, rivets, liquid adhesiv..
Tensile Strength, Yield	0.830 MPa	120 psi	508 mm/min; ASTM D638
Dow Engage® 8842 Polyolefin Elastomer Description: Engage® 8842 polyolefin elastomer is an ultra-low density ethylene-octene copolymer with a nominal loose talc surface coating. The talc is untreated and has a nominal 1 µm particle si..