Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 885 MPa @Strain 0.200 %, Temperature 650 °C |
128000 psi @Strain 0.200 %, Temperature 1200 °F |
|
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | >= 880 MPa | >= 128000 psi | |
MetalTek MTEK 535 Martensitic Stainless Steel Information provided by MetalTek |
|||
Tensile Strength, Yield | 885 MPa @Strain 0.200 % |
128000 psi @Strain 0.200 % |
Typical |
TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Rod Medium To High Strength General-Purpose Alloy. Tensile property data below is typical of rod; more specific form/thickness entries are also available in MatWeb.Industry Specifications: USA Aeros.. |
|||
Tensile Strength, Yield | 880 MPa @Strain 0.200 % |
128000 psi @Strain 0.200 % |
Typical |
TIMET TIMETAL® 21S Titanium Alloy (Ti-15Mo-3Nb-3Al-0.2Si, ASTM Grade 21); Annealed Strip/Sheet High-Strength, Oxidation Resistant Strip AlloyFeatures: Offers the good cold formability and weldability of a beta strip alloy, but with greatly improved oxidation resistance and creep strength. Aer.. |
|||
Tensile Strength, Yield | 882 MPa @Temperature 23.0 °C |
128000 psi @Temperature 73.4 °F |
0°, Conditioning: 23°C; ASTM D3039 |
Hexcel® HexPly® M49 120°C Curing Epoxy Matrix, 3K High Strength Carbon Fiber Designation: C280T4; Twill 4x4Information provided by HexCel |
|||
Tensile Strength, Yield | 880 MPa | 128000 psi | |
Elgiloy® Co-Cr-Ni Alloy, Wire, 20% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
Tensile Strength, Yield | 883 MPa @Strain 0.200 % |
128000 psi @Strain 0.200 % |
|
Carpenter BioDur™ 316LS Stainless Medical Implant Alloy, 60% Cold Worked Data provided by Carpenter Technology Corporation.Medical Implant Alloy. Vacuum arc remelted (VAR), low carbon version of Type 316 stainless. The secondary premium melting step (VAR) imparts impro.. |
|||
Tensile Strength, Yield | 882 MPa @Strain 0.200 % |
128000 psi @Strain 0.200 % |
|
Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1093°C 1 hr Data provided by Carpenter Technology Corporation.Annealing followed by water quench and low stress grinding prior to tensile testing.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting h.. |
|||
Tensile Strength, Yield | 883 MPa @Strain 0.200 %, Temperature -73.0 °C |
128000 psi @Strain 0.200 %, Temperature -99.4 °F |
|
Carpenter Custom 450® Stainless Steel, Annealed Data provided by Carpenter Technology Corporation.Custom 450® stainless is a martensitic age-hardenable stainless steel which exhibits very good corrosion resistance (similar to that of Stainless T.. |
|||
Tensile Strength, Yield | 883 MPa @Strain 0.200 % |
128000 psi @Strain 0.200 % |
|
Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 732°C/8hr/FC to 621°C/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |
|||
Tensile Strength, Yield | 882 MPa | 128000 psi | Hardened 1800°F, Tempered 1000°F |
ATI Allegheny Ludlum 410 Martensitic Stainless Steel Characteristics: superior wear resistance, hardenable, excellent corrosion resistance. Applications:cutlery, dental and surgical instruments, nozzles, valve parts, hardened steel ball and seats for.. |
|||
Tensile Strength, Yield | 882 MPa @Strain 0.200 % |
128000 psi @Strain 0.200 % |
typical |
ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 538°C Temper Allegheny Ludlum Type 410 is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainles.. |