Polymer Property : Tensile Strength, Yield = 132000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	910 MPa @Strain 0.200 %, Temperature 315 Â°C	132000 psi @Strain 0.200 %, Temperature 599 Â°F
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595Â°C (1100Â°F) for 2 hours Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Yield	910 MPa @Strain 0.200 %	132000 psi @Strain 0.200 %
Haynes Waspaloyâ„¢ alloy, sheet Age-hardenable superalloy with very good strength at temperatures up 980Â°C (1800Â°F), can be cold-formed in the annealed condition, may also be hot formed at 1040Â°C (1900Â°F) and above, go..
Tensile Strength, Yield	910 MPa	132000 psi
Kinetics MIM 17-4PH Stainless Steel (H1100 Condition) Precipitation-hardening stainless steel. Offers a good balance between corrosion resistance and strength. Magnetic. Hardenable to various strength levels and hardness by varying the aging heat treat..
Tensile Strength, Yield	910 MPa @Strain 0.200 %	132000 psi @Strain 0.200 %	Typical
TIMET TIMETAL® 1100 Titanium Alloy (Ti-6Al-2.7Sn-4Zr-0.4Mo-0.45Si) Features: A near alpha, high temperature creep resistant alloy developed for elevated temperature use in the range of 600°C that offers the highest combination of strength, creep resistance, fractu..
Tensile Strength, Yield	910 - 1000 MPa @Strain 0.200 %	132000 - 145000 psi @Strain 0.200 %
CLAL-MSX DECLAFOR® 1015 THX Rod quenched/Cold Rolled/Precipitation Heat Treated Copper Alloy Main Characteristic: Age hardening alloyBeriyllium free alloyGood machinabilityHigh mechanical propertiesTypical Applications:Coaxial connectorsSpectacles partsSliding contacts partsAll kind of turn..
Tensile Strength, Yield	910 - 958 MPa	132000 - 139000 psi	Rp 0.2
Arcam Ti6Al4V Titanium Alloy Ti6Al4V is the most widely used titanium alloy and has numerous applications in the medical industry, aerospace, automotive and marine equipment industry. Ti6Al4V ELI features Extra Low Interstitial..
Tensile Strength, Yield	910 MPa @Strain 0.200 %, Temperature 427 °C	132000 psi @Strain 0.200 %, Temperature 801 °F
Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Condition H 900 (Age-Hardened 482°C/1hr/AC) Data provided by Carpenter Technology Corporation.Custom 630 (17Cr-4Ni) is a martensitic precipitation/age-hardening stainless steel offering high strength and hardness along with excellent corrosio..