Polymer Property : Tensile Strength, Yield = 133000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	920 MPa	133000 psi
Industeel SuperplastÂ® SP300 Prehardened Mold Steel SuperplastÂ® 300 (SP300) is a prehardened steel with a BHN 300 (32 HRC) to be used for plastic injection molds, extrusion dies, and compression molds offering improved performance for the mold mak..
Tensile Strength, Yield	915 MPa @Strain 0.200 %	133000 psi @Strain 0.200 %
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Yield	920 MPa @Strain 0.200 %	133000 psi @Strain 0.200 %
Haynes 230Â® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Yield	915 MPa @Strain 0.200 %, Temperature 540 Â°C	133000 psi @Strain 0.200 %, Temperature 1000 Â°F
Haynes 25 alloy, cold worked sheet, 20 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Yield	>= 920 MPa	>= 133000 psi	50<x=60mm
ThyssenKrupp XABO® 960 Structural Steel This Material Specification applies to liquid-quenched and tempered heavy plates from 3 up to 100 mm in thickness, made of the high-strength special structural steels XABO® 890 and XABO® 960.Appli..
Tensile Strength, Yield	920 MPa @Temperature 23.0 °C	133000 psi @Temperature 73.4 °F	0º, Conditioning: 23°C; ASTM D3039
Hexcel® HexPly® M47 140°C Curing Epoxy Matrix, Woven Carbon Prepreg 42% resin weight with C193PW(HTA) - 193 g/m2 plain weave 3K HTA 49% fiber volumeInformation provided by HexCel
Tensile Strength, Yield	917 MPa @Strain 0.200 %, Temperature 199 °C	133000 psi @Strain 0.200 %, Temperature 390 °F	hardened to 350 HB
Bohler-Uddeholm BÖHLER RAMAX® HH Modified 420F Chromium alloyed steelTypical applications for Ramax® HH are: holders and bolsters for plastic molds, plastic and rubber molds with low requirements on polishability, and dies for plastic extrusion..
Tensile Strength, Yield	916 MPa	133000 psi	Hardened 1800°F, Tempered 800°F
ATI Allegheny Ludlum 410 Martensitic Stainless Steel Characteristics: superior wear resistance, hardenable, excellent corrosion resistance. Applications:cutlery, dental and surgical instruments, nozzles, valve parts, hardened steel ball and seats for..
Tensile Strength, Yield	916 MPa @Strain 0.200 %	133000 psi @Strain 0.200 %	typical
ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 427°C Temper Allegheny Ludlum Type 410 is a hardenable straight-chromium stainless steel which combines superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainles..