Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 50 mm/min; ASTM D638 |
Ovation Polymers Nima™ HL 30525 GF FR PET, 25% Glass Fiber PET – Flame Retardant 25% Short Glass Fiber Reinforced. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to ASTM s.. |
|||
Tensile Strength, Yield | 98.1 MPa | 14200 psi | 23°C; 50% RH; ASTM D638 |
PTS Lucet® GC-225 25% Glass Reinforced Acetal Copolymer Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength, Yield | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical LUPOS GP2206F ABS+GF20%, Flame Retardant Feature: Injection Molding, ABS+GF20%, Flame RetardantApplication: Electric & Electronic (Housing, Components)CAS No. 9003-56-9, 9003-54-7, 65997-17-3, 88497-56-7 and 1309-64-4Information provided b.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp GFL14 PSU LNP* Lubricomp* GFL14 is a compound based on Polysulfone containing Glass Fiber and PTFE Lubricant.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem DT1800E PEI Blend Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Americas re.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem DT1800E PEI Blend (Asia Pacific) Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacifi.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem DT1800E PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Afri.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem DT1810E PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacifi.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem DT1810E PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Afri.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM DT1810EV PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem DT1810EV PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed.This data was supplied by SABIC-IP for.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM EXUM0167 PEI Blend Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem EXUM0169 PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Afri.. |
|||
Tensile Strength, Yield | 98.1 MPa | 14200 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® EM-8250G MPPE, 20% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 98.1 MPa | 14200 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® TK-6036H PPA, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 98.1 MPa | 14200 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® EM-8250G MPPE, 20% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 98.1 MPa | 14200 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® GP-5150GT PBT, 15% Glass Filled Low warpage with 15% GF reinforcement and can be used in the switches for microwave or ovensInformation provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL CN1134 PPE+PS (Asia Pacific) 20% filled FR high modulus PPE/PS blend |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP (Europe-Africa-Middle East) Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL PPX ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
Tensile Strength, Yield | 97.9 MPa | 14200 psi | ASTM D638 |
A. Schulman ComAlloy® E-14961 30% Glass Fiber Reinforced Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Yield | 97.9 MPa | 14200 psi | ASTM D638 |
A. Schulman ComAlloy® E-14961 30% Glass Fiber Reinforced Polycarbonate Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | ISO value at 50 mm/min. |
BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron HPN 9333G HS is a heat stabilized, 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with.. |
|||
Tensile Strength, Yield | 98.1 - 216 MPa | 14200 - 31300 psi | Average value: 145 MPa Grade Count:4 |
Overview of materials for Polyphthalamide (PPA), 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are .. |
|||
Tensile Strength, Yield | 97.9 - 112 MPa | 14200 - 16200 psi | Average value: 107 MPa Grade Count:3 |
Overview of materials for Polysulfone, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are inc.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
SABIC Innovative Plastics Lexan® LC108 PC (Asia Pacific) Polycarbonate base, 8% carbon fiber reinforced, FR |
|||
Tensile Strength, Yield | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical LUCON CP6067 PC+CNT+CF Description: Injection Molding, PC+CNT+CF, Electrostatic Dissipation, High Strength, High Flow & Good ProcessabilityApplication: Wafer Carrier Box, Conveyor belt bearing blockCAS No. 103598-77-2, 74.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | ISO 527 |
Victrex® PEEK 381G Medium Viscosity Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, depth filtered granules for specialty extrusion processes, standard flow, FD.. |
|||
Tensile Strength, Yield | 98.0 MPa @Temperature 23.0 °C |
14200 psi @Temperature 73.4 °F |
ISO 527 |
Victrex® PEEK 450G903 Black Polyetheretherketone, Unreinforced Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, FDA food contac.. |