Polymer Property : Tensile Strength, Yield = 39200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	270 MPa @Strain 0.200 %, Temperature 871 Â°C	39200 psi @Strain 0.200 %, Temperature 1600 Â°F
Kennametal Stellite StelliteÂ® 6B solution heat-treated at 1232Â°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and..
Tensile Strength, Yield	270 MPa @Strain 0.200 %, Temperature 760 Â°C	39200 psi @Strain 0.200 %, Temperature 1400 Â°F
Haynes 188 alloy, hot rolled and 1175Â°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Yield	>= 270 MPa	>= 39200 psi
MetalTek MTEK 29-10 Cast UNS J93403 Heat Resistant Stainless Steel Higher chrome and nickel bring greater strength and ductility.Applications: Furnace chains, ore roasting equipment.Information provided by MetalTek
Tensile Strength, Yield	270 MPa @Strain 0.200 %, Temperature 760 Â°C	39200 psi @Strain 0.200 %, Temperature 1400 Â°F
Haynes 188 alloy, cold rolled and 1175Â°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Yield	270 MPa @Strain 0.200 %, Temperature 540 Â°C	39200 psi @Strain 0.200 %, Temperature 1000 Â°F
Haynes HastelloyÂ® B-3Â® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOYÂ® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Tensile Strength, Yield	270 MPa @Strain 0.200 %, Temperature 550 Â°C	39200 psi @Strain 0.200 %, Temperature 1020 Â°F	Annealed prior to test
Special Metals BRIGHTRAYÂ® Alloy F Electrical Resistance Alloy A nickel-iron-chromium electrical-resistance alloy for use at temperatures up to 1920Â°F (1050Â°C) under continuous operating conditions. Its high iron content and relatively low level of nicke..
Tensile Strength, Yield	270 MPa	39200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP LX08411 PEEK LNP* THERMOCOMP* LX08411 is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added feature of this material is: Opaque.
Tensile Strength, Yield	270 MPa @Temperature 75.0 °C	39200 psi @Temperature 167 °F	Wet; EN2561
Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, 37%/7781 Fiber Information provided by HexCel
Tensile Strength, Yield	270 MPa @Temperature 100 °C	39200 psi @Temperature 212 °F	Wet; EN2561
Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, 37%/7781 Fiber Information provided by HexCel
Tensile Strength, Yield	270 MPa @Temperature 75.0 °C	39200 psi @Temperature 167 °F	90º, Wet; EN2561
Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, 37%/7781 Fiber Information provided by HexCel
Tensile Strength, Yield	270 MPa	39200 psi
AK Steel Hot Rolled Carbon Steel, Commercial Steel (CS Type B), Standard Grade May be moderately formed. A specimen cut in any direction can be bent flat on itself without cracking.Information provided by AK Steel
Tensile Strength, Yield	270 MPa	39200 psi
Ametek Ultra 303L P/M Stainless Steel, Sintered from 6.65 g/cc Green Density Ametek's patented Ultra Stainless Steels™ are produced by alloying the conventional austenitic compositions with a small amount of a copper-nickel-tin alloy. This results in a marked improvement i..
Tensile Strength, Yield	270 MPa	39200 psi
Ametek Ultra 316L P/M Stainless Steel, Sintered from 6.8 g/cc Green Density Ametek's patented Ultra Stainless Steels™ are produced by alloying the conventional austenitic compositions with a small amount of a copper-nickel-tin alloy. This results in a marked improvement i..
Tensile Strength, Yield	270 MPa @Strain 0.200 %, Temperature 649 °C	39200 psi @Strain 0.200 %, Temperature 1200 °F
Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..