Polymer Property : Tensile Strength, Yield = 660 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Yield	660 MPa @Strain 0.200 %, Temperature 760 Â°C	95700 psi @Strain 0.200 %, Temperature 1400 Â°F
Haynes 25 alloy, cold worked sheet, 20 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Yield	660 MPa @Strain 0.200 %	95700 psi @Strain 0.200 %
Haynes 625 alloy, plate after 1000 hours at 760Â°C (1400Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Yield	>= 660 MPa @Strain 0.200 %	>= 95700 psi @Strain 0.200 %
CLAL-MSX DECLAFOR® 1015 TDX Wire quenched/Cold Rolled Copper Alloy Main Characteristic: Age hardening alloyBeriyllium free alloyGood machinabilityHigh mechanical propertiesTypical Applications:Coaxial connectorsSpectacles partsSliding contacts partsAll kind of turn..
Tensile Strength, Yield	660 MPa	95700 psi
Ametek 17-4 P/M Process, Sintered at 2300°F (1260°C) Composition reported is typical of 17-4 precipitation hardening stainless. This alloy is widely used because of its high strength, high hardness, excellent corrosion resistance, and easy heat treat..
Tensile Strength, Yield	660 - 830 MPa	95700 - 120000 psi
ArcelorMittal Dual Phase 980 LCE Y660 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft ..