Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 680 - 830 MPa | 98600 - 120000 psi | |
Materion Beryllium Copper Alloy 10 Plate & Rolled Bar; HT (TH04) Temper; up to 76 mm Thickness (UNS C17500) Treatment required for max strength: 2 hrs @ 480°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In.. |
|||
Tensile Strength, Yield | 680 - 830 MPa | 98600 - 120000 psi | |
Materion Beryllium Copper Alloy 3 Plate & Rolled Bar; HT (TH04) Temper; up to 76 mm Thickness (UNS C17510) Treatment required for max strength: 2 hrs @ 480°C or Mill HardenedTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials In.. |
|||
Tensile Strength, Yield | 760 - 830 MPa @Strain 0.200 % |
110000 - 120000 psi @Strain 0.200 % |
|
CLAL-MSX DECLAFOR® 1015 TH2 Wire quenched/Precipitation Heat Treated Copper Alloy Main Characteristic: Age hardening alloyBeriyllium free alloyGood machinabilityHigh mechanical propertiesTypical Applications:Coaxial connectorsSpectacles partsSliding contacts partsAll kind of turn.. |
|||
Tensile Strength, Yield | 660 - 830 MPa | 95700 - 120000 psi | |
ArcelorMittal Dual Phase 980 LCE Y660 Very high strength steel, Cold Rolled Steel Description: Dual Phase steels offer an outstanding combination of strength and drawability as a result of their microstructure, in which a hard martensitic or bainitic phase is dispersed in a soft .. |
|||
Tensile Strength, Yield | 680 - 830 MPa | 98600 - 120000 psi | |
ArcelorMittal Complex Phase Steel 800 Very high strength steel, Hot Rolled Steel Available in the following: uncoated (HCT780C) and Extragal®/Galvannealed (HCT780C+Z)Description: The Complex Phase family of steels supplements ArcelorMittal's VHSS (very high strength steel) prod.. |
|||
Tensile Strength, Yield | 650 - 830 MPa | 94300 - 120000 psi | |
Materion Beryllium Copper Alloy 3 Strip; HT (TH04) Temper (UNS C17510) Treatment required for max strength: 2-3 hrs @ 480ºC or Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 96%Stress Relaxation after 1000 hrs @ 200°C: 75%Formability Ratio.. |