Polymer Property : Tensile Strength, Yield = 77600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English
Tensile Strength, Yield	535 MPa @Strain 0.200 %, Temperature 760 Â°C	77600 psi @Strain 0.200 %, Temperature 1400 Â°F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079Â°C, water quenched, 30 minutes at 1066Â°C, air cooled, aged 16 hours at 760Â°C (1400Â°F) Vacuum melted, exceptionally high strength at temperature between 649-982Â°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Tensile Strength, Yield	535 MPa @Strain 0.200 %	77600 psi @Strain 0.200 %
Haynes 25 alloy, room temperature sheet after 500 hours of 870Â°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Yield	535 MPa @Strain 0.200 %	77600 psi @Strain 0.200 %
Special Metals INCONELÂ® 625LCFÂ® Nickel Superalloy (UNS N06626) Annealed 1950Â°F (1070Â°C) Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 1950Â°F (1070Â°C)/5 minutes/AC. This produces ASTM grain size 9.5. Other property values are ty..
Tensile Strength, Yield	535 MPa @Strain 0.200 %	77600 psi @Strain 0.200 %
Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Yield	535 MPa @Strain 0.200 %	77600 psi @Strain 0.200 %
Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..