Polymer Property : Tensile Modulus = 2.06 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	2.06 GPa	299 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics Cycolac® FR15U ABS Flame retardant ABS with excellent indoor UV properties and excellent processing. UL94 V-0/5VA rated. Elevated UL RTI rating (90-85-90) for all colors except for blue and green colors (60-60-60).
Tensile Modulus	2.06 GPa	299 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics Cycolac® MGABS01 ABS Injection molding ABS. High impact, high gloss, good flow.
Tensile Modulus	2.06 GPa	299 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics Cycolac® X11 ABS Automotive: High heat resistance. Excellent flow/impact balance. UL94 HB rated. High gloss.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics Cycoloy® MC8100 PC+ABS (Asia Pacific) Extrusion blowmolding grade.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Colorcomp D10009 PC LNP* Colorcomp* D10009 is a compound based on Polycarbonate resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant.This data was supplied ..
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Colorcomp D10009 PC (Asia Pacific) LNP* Colorcomp* D10009 is a compound based on Polycarbonate resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant.This data was supplied ..
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP COLORCOMP D1000P PC (Asia Pacific) LNP* Colorcomp* D1000P is a compound based on Polycarbonate resin containing Unfilled Custom Color. Added features of this material include: Exceptional Processing.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DL001 PC LNP* LUBRICOMP* DL001 is a compound based on Polycarbonate resin containing 5% PTFE. Added features of this material include: Internally Lubricated.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DL001 PC (Asia Pacific) LNP* Lubricomp* DL001 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DL002ER PC LNP* Lubricomp* DL002ER is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Internally Lubricated, Easy Molding, Mold Release.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DL003 PC (Asia Pacific) LNP LUBRICOMP* DL003 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated.
Tensile Modulus	2.06 GPa @Thickness 3.20 mm	299 ksi @Thickness 0.126 in	1 mm/min; ASTM D638
LG Chemical AF360 ABS, TBBA-free Flame Retardant Feature: Injection Molding, TBBA-free Flame RetardantApplication: Electric/Electronic Applications (TV, Monitor Housing) IT/OA deviceCAS No. 9003-56-9, 84852-53-9 and 1309-64-4Information provided b..
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DX98306H PC (Asia Pacific) LNP* Lubricomp* DX98306H is a compound based on Polycarbonate resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Lubricomp GL004 PSU (Asia Pacific) LNP* Lubricomp* GL004 is a compound based on Polysulfone resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pacifi..
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP IL004 PA 6/12 LNP* LUBRICOMP* IL004 is a compound based on Nylon 6/12 resin containing 20% PTFE. Added features of this material include: Wear Resistant.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP KP004L Acetal Copoly (Asia Pacific) LNP* Lubricomp* KP004L is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP ZL003 PPE+PS LNP* LUBRICOMP* ZL003 is a compound based on PPE+PS resin containing 15% PTFE. Added features of this material include: Wear Resistant.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRILOY D20009P PC LNP* LUBRILOY* D20009P is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Flame Retardant, Exceptional Processing...
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRILOY K2000 Acetal LNP LUBRILOY* K2000 is a compound based on Acetal resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-LOY A3000 ABS LNP STAT-LOY* A3000 is a compound based on ABS resin. Added feature of this material is: Antistatic.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-LOY A30009 ABS (Asia Pacific) LNP* Stat-loy* A30009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant. Added features of this material include: Antistat, Flame Retardant.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
Samsung Cheil Industries InfinoÂ® HI-1001BN PC/ABS, Unreinforced PC/ABS that is used for the housing of mobile phone, wheel cap, rice cooker, electric iron etc., refrigerator door handle, panel etc.Information provided by Samsung Cheil Industries.
Tensile Modulus	2.06 GPa	299 ksi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® SF-0505HWR MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries.
Tensile Modulus	2.06 GPa	299 ksi	5 mm/min; ASTM D638
Samsung Cheil Industries StarexÂ® SF-0505HWR MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP MB008S PP LNP* THERMOCOMP* MB008S is a compound based on Polypropylene resin containing 40% Glass Bead. Added features of this material include: Heat Stabilized.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp MB008S PP (Asia Pacific) LNP* Thermocomp* MB008S is a compound based on Polypropylene resin containing Glass Bead. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Pa..
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl MX5569 PPE+PS PPE+PS blend. High Heat. Good balance of flow and impact. Offers good aging performance under heat. Typical applications include Automotive Interiors and Lighting.This data was supplied by SABIC-..
Tensile Modulus	2.06 GPa @Temperature -70.0 °C	299 ksi @Temperature -94.0 °F	DAM; Dynamic; ISO 11403-1 -2
DuPont Performance Polymers Zytel® 330 NC010 Nylon (Unverified Data**) Unreinforced PolyamideZytel 330 NC010 is a transparent polyamide resin with amorphous characteristics.Information provided by DuPont Performance Polymers
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DBL32 PC (Asia Pacific) LNP* Lubricomp* DBL32 is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated.
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Lubricomp GL004 PSU LNP* Lubricomp* GL004 is a compound based on Polysulfone resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas re..