SABIC Innovative Plastics LNP LUBRICOMP DL001 PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DL001 PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* DL001 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
ASTM D792
1.22 g/cc
0.0441 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0078 cm/cm

@Time 86400 sec
0.0078 in/in

@Time 24.0 hour
ISO 294
0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0096 cm/cm

@Time 86400 sec
0.0096 in/in

@Time 24.0 hour
ISO 294
0.0090 - 0.011 cm/cm

@Time 86400 sec
0.0090 - 0.011 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 51.0 MPa
7400 psi
ASTM D638
53.0 MPa
7690 psi
ISO 527
Tensile Strength, Yield 54.0 MPa
7830 psi
ISO 527
56.0 MPa
8120 psi
ASTM D638
Elongation at Break 76.6 %
76.6 %
ASTM D638
167 %
167 %
ISO 527
Elongation at Yield 6.0 %
6.0 %
ISO 527
6.2 %
6.2 %
ASTM D638
Tensile Modulus 2.06 GPa
299 ksi
50 mm/min; ASTM D638
2.19 GPa
318 ksi
1 mm/min; ISO 527
Flexural Strength 70.0 MPa
10200 psi
ISO 178
Flexural Modulus 2.06 GPa
299 ksi
ASTM D790
2.10 GPa
305 ksi
ISO 178
Izod Impact, Notched 1.60 J/cm
3.00 ft-lb/in
ASTM D256
Izod Impact, Unnotched 24.19 J/cm
45.32 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 176 kJ/m²
83.7 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 39.0 J
28.8 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 49.0 J
36.1 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.39
0.39
ASTM D3702 Modified
Coefficient of Friction, Static 0.32
0.32
ASTM D3702 Modified
K (wear) Factor 183 x 10-8 mm³/N-M
91.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 73.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
74.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
76.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 142 °C
288 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
142 °C

@Thickness 3.20 mm
288 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
264 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
132 °C

@Thickness 3.20 mm
270 °F

@Thickness 0.126 in
unannealed; ASTM D648