Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 9.51 GPa | 1380 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP DF006ER PC LNP THERMOCOMP* DF006ER is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Mold Release. |
|||
Tensile Modulus | 9.51 GPa | 1380 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP WF006U PBT (Asia Pacific) LNP* THERMOCOMP* WF006U is a compound based on Polybutylene Terephalate resin containing Glass Fiber. Added features of this material include: UV Stabilized. |
|||
Tensile Modulus | 9.51 GPa | 1380 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP WF006U PBT LNP* THERMOCOMP* WF006U is a compound based on PBT resin containing 30% Glass Fiber. Added feature of this material is: UV Stabilized. |
|||
Tensile Modulus | 9.51 GPa | 1380 ksi | ASTM D638 |
Ensinger TECATRON™ PVX Polyphenylene sulfide (PPS), Bearing Grade TECATRON PPS is a high performance thermoplastic that combines good mechanical properties with excellent thermal and chemical resistance properties. There is no known solvent that dissolves TECATRON.. |
|||
Tensile Modulus | 9.51 GPa | 1380 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP VERTON PX00700 PA 6 LNP VERTON* PX00700 is a compound based on Nylon 6 resin containing proprietary fillers. Added feature of this grade is: Structural. |
|||
Tensile Modulus | 9.51 GPa | 1380 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP VERTON PX00700 PA 6 (Asia Pacific) LNP* Verton* PX00700 is a compound based on Nylon 6 resin containing Long Glass Fiber. |